BiFeO 3 -Bi ( Zn 1 / 2 Ti 1 / 2 ) O 3 (BF-BZT) ceramics were made by a solid state reaction method. Crystal structure and microstructure were observed. Leakage currents were much reduced with BZT doping in BF. Dielectric constants of BF-BZT increased as frequency is decreased. Two distinctive relaxations were observed at about 500 kHz and 3 Hz. Ferroelectriclike hysteresis loops were observed in BF with low electric field and 2.5 and 5 mol % BZT doped ceramics.
K nonstoichiometry effects in (Bi 0.5 K 0.5+x )TiO 3 (BKT) ceramics were studied with K contents varying in the range of −8≤ x ≤+1 mol% from the stoichiometric K 0.5 . Within the range tested, a single BKT phase region was found to be at −1≤ x ≤+1 mol% and secondary phases started emerging with further K deficiency. Despite the formation of secondary phases, BKT perovskite with tetragonal symmetry was retained at all compositions. For nonstoichiometric BKT perovskite, a composition dependent structure property relation was observed; a decrease in tetragonality (c/a) caused piezoelectric coefficient (d 33 ) enhanced while depolarization temperature (T d ) reduced and vice versa.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.