Crystallographic textures of the austenitic low-density Fe-30.5Mn-8.0Al-1.2C (8Al) and Fe-30.5Mn-2.1Al-1.2C (2Al) (wt.%) steels were examined during cold rolling by means of electron backscatter diffraction (EBSD) and electron channeling contrast imaging (ECCI). Random oriented grains orient towards Goss-and brass-components along the α-fiber as the strain increased, with activation of slip, mechanical twinning, and shear banding, for both steels. S-and copper-orientations were also observed in the 8Al steel at 50% reduction. The route of Cu-CuT-Gossbrass texture evolution was found in the 2Al alloy. Cu, Goss, and brass textures occur as a dominant texture in the deformed 8Al alloy. Copper-type texture accompanied with slip at low reduction (20%), as well as Cu-type shear bands, and shear banding inside Goss-oriented grains at higher reduction (50%), were observed in the 8Al steel. It is suggested that this copper-type rolling texture may be attributed to the Al addition, which contributes to its low twinning activity compared to that in the 2Al alloy. Cu-CuT-brass f.c.c. rolling texture transition to form the Brass-type texture was observed at higher reduction in the 2Al alloy with strong similarity to that found in other Fe-Mn-C system TWIP steels.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.