Aluminum matrix composites (AMC) are of great interest and importance as high-performance materials with enhanced mechanical properties. Al2O3 is a commonly used reinforcement in AMCs fabricated by means of various technological methods, including casting and sintering. Selective laser melting (SLM) is a suitable modern method of the fabrication of net-shape fully dense parts from AMC with alumina. The main results, achievements, and difficulties of SLM applied to AMCs with alumina are discussed in this review and compared with conventional methods. It was shown that the initial powder preparation, namely the particle size distribution, sphericity, and thorough mixing, affected the final microstructure and properties of SLMed materials drastically. The distribution of reinforcing particles tends to consolidate the near-melting pool-edges process because of pushing by the liquid–solid interface during the solidification process that is a common problem of various fabrication methods. The achievement of an homogeneous distribution was shown to be possible through both the thorough mixing of the initial powders and the precise optimization of SLM parameters. The strength of the AMCs fabricated by the SLM method was relatively low compared with materials produced by conventional methods, while for superior relative densities of more than 99%, hardness and tribological properties were obtained, making SLM a promising method for the Al-based matrix composites with Al2O3.

No abstract

Rare-earth (R)-iron alloys are a backbone of permanent magnets. Recent increase in price of rare earths has pushed the industry to seek ways to reduce the R-content in the hard magnetic materials. For this reason strong magnets with the ThMn12 type of structure came into focus. Functional properties of R(Fe,T)12 (T-element stabilizes the structure) compounds or their interstitially modified derivatives, R(Fe,T)12-X (X is an atom of hydrogen or nitrogen) are determined by the crystal-electric-field (CEF) and exchange interaction (EI) parameters. We have calculated the parameters using high-field magnetization data. We choose the ferrimagnetic Tm-containing compounds, which are most sensitive to magnetic field and demonstrate that TmFe11Ti-H reaches the ferromagnetic state in the magnetic field of 52 T. Knowledge of exact CEF and EI parameters and their variation in the compounds modified by the interstitial atoms is a cornerstone of the quest for hard magnetic materials with low rare-earth content.

No abstract

This work aims to study the possibility of using an electrostatic drum-type separator to prepare a powder with a narrow size distribution curve for usage in additive manufacturing. The size distributions of the uncoated commercial aluminum powders ASP-30, ASP-22, and ASP-5 were analyzed. It was shown that the powders ASP-30 and ASP-22 have similar asymmetric distributions with a SPAN of 1.480 and 1.756, respectively. ASP-5 powder, in turn, has a narrow distribution with a SPAN of 0.869. ASP-30 powder was chosen for further experiment because, traditionally, separators are used to classify large-sized materials with particle size more than 100 μm. The optimal mode of electrostatic classification was proposed for the selected powder. Various classification methods, including centrifugal and electrostatic, were compared. The powders before and after classification were studied by XRD, SEM, TEM, and TG–DSC analyses. The obtained results showed that electrostatic classification does not lead to the formation of coatings on the processed powders. Electrostatic separation effectively narrows the particle size distribution, making it a suitable and valuable method to classify initial powders for additive manufacturing.

The article presents a detailed study and characterization of the oxide layers on the surface of iron particles of various sizes. Ten iron samples with a size range from a few nm to 50 µm were studied in detail using SEM, TEM, XRD, and TGA analysis. The composition of the multiphase oxide layers on the powder surface was investigated. The main components of the oxide layer were FeO, Fe3O4, and Fe2O3. By the obtained data, a model for the calculation of a multiphase oxide layer thickness on the surface of iron particles was proposed. The proposed model was validated and can be used for the characterization and certification of micro– and nanoscale iron particles.

The study is devoted to X-ray fluorescence spectroscopy (XRF) features of micro- and nanosized powder mixtures of copper and nickel. XRF is a high accuracy method that allows for both qualitative and quantitative analysis. However, the XRF measurement error due to the size of the studied particles is not usually taken into account, which limits the use of the method in some cases, such as analysis of Ni-Cu mixtures and coatings. In this paper, a method for obtaining copper and nickel nanoparticles was investigated, and the XRF of powder compositions was considered in detail. The initial micro- and nanoparticles of copper and nickel were studied in detail using SEM, TEM, XRD, and EDX. Based on experimental data, calibration curves for copper-nickel powder compositions of various sizes were developed. According to the results, it was experimentally established that the calibration curves constructed for nanoscale and microscale powders differ significantly. The presented approach can be expanded for other metals and particle sizes.

Laser powder bed fusion (LPBF) of Cu-0.5Cr was carried out using recycled powder taken out from the LPBF machine after previous printing. Various volumetric defects characterized the powder wherein particle size distribution was the same as virgin powder. Using recycled powder resulted in extra spherical pore formation after the LPBF process. Despite that, a relative density of 99.2% was achieved by LPBF parameters optimization. Solidified microstructure with a small volume of defects consisted of an oversaturated dendritic Cu matrix and nano-sized Cr precipitations providing strengthening mechanism occurrence. The possibility of a satisfactory level of mechanical properties with σ0.2 = 136.8 MPa, UTS = 187.4 MPa, along with 15.5% of elongation achieving, was shown.