In this paper, the oxy-fluorination process and the influence of different concentrations of fluorine and oxygen in the gas phase on the physicochemical properties of polyacrylonitrile(PAN)-based carbon fibers are described. The properties of the treated carbon structures are determined by zeta potential and tensiometry measurements. In addition, changes in surface composition and morphology are investigated by X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM). Adhesion properties are characterized by the single fiber pull-out (SFPO) test. Furthermore, changes in intrinsic properties are described by means of tensile and density measurements. After a primary desizing effect by oxy-fluorination, an increased number of oxygen-containing surface functional groups could be detected, which led to more debonding work in SFPOs with an epoxy-based matrix. It was also shown that the polar surface energy grows with rising fluorine concentration in the reaction gas mixture. In addition, a minor increase of ~10% in the maximum strength of PAN-based carbon fibers is detected by single fiber tensile measurements after oxy-fluorination with a fluorine content of 5% in the reaction mixture.
Non-crimp fabrics (NCF) have become established in the fields of the automotive, aircraft, and wind power industries, which has led to an increasing demand of fiber plastic composites. In order to utilize the known excellent load-bearing properties of NCF and also to reduce the related disadvantages such as fiber undulation caused by stitching yarn, inclusions of resin and filament breakage by the stitch-bonding process have to be addressed. Hence, an alternative manufacturing technology is presented. This technology is defined by the punctiform application of a polyester hot melt adhesive to enable different geometries of NCF and ensure the position of the high-performance fiber in the load direction. The new manufacturing process, on the one hand, demands new testing methods to investigate the adhesion between the used adhesive and high-performance fibers, while, on the other, the surface of the adherend (carbon fiber) needs to be improved. Oxyfluorination is used here for the surface modification. Different tests such as peel test, shear test and transverse tensile test were developed and evaluated with different adhesives and high-performance yarns based on glass and carbon. The influence of the used copolyester hot melt on the curing kinetics of an epoxy matrix was investigated by differential scanning calorimetry using quasi-isothermal and non-isothermal measurements. In addition, the interface between the thermoplastic epoxy resin and the copolyester hot melt was analyzed by scanning electron microscopy.
Abstract:In this work, typical high-performance yarns are oxy-fluorinated, such as carbon fibers, ultra-high-molecular-weight polyethylene, poly(p-phenylene sulfide) and poly(p-phenylene terephthalamide). The focus is on the property changes of the fiber surface, especially the wetting behavior, structure and chemical composition. Therefore, contact angle, XPS and tensile strength measurements are performed on treated and untreated fibers, while SEM is utilized to evaluate the surface structure. Different results for the fiber materials are observed. While polyethylene exhibits a relevant impact on both surface and bulk properties, polyphenylene terephthalamide and polyphenylene sulfide are only affected slightly by (oxy-)fluorination. The wetting of carbon fiber needs higher treatment intensities, but in contrast to the organic fibers, even its textile-physical properties are enhanced by the treatment. Based on these findings, the capability of (oxy-)fluorination to improve the adhesion of textiles in fiber-reinforced composite materials can be derived.
In this paper, a method for the evaluation of the influence of different polymer suspensions and environmental conditions on adhesion between an impregnated carbon fibre heavy tow and concrete for reinforcement will be proposed. For this purpose, the impregnation material itself was investigated as a polymer film before and after incubation in water and aqueous suspensions, such as NaOH and a cementitious solution, in terms of its thermal properties, swelling behaviour and morphology. Thin polymer films were manufactured and subsequently investigated with quantification of the swelling for 28 d by thermal and scanning electron microscope analysis. The effect of pull-out shear stress was evaluated to investigate parameters such as high temperature and moisture on adhesion to concrete. Contact angle measurements were used to determine the surface energy of the polymer films. All incubated polymer films yielded a change in both surface morphology and specific residues on the polymer film surface, e.g. in the form of calcium carbonate, but no change in glass-transition temperature. A high correlation between glass-transition temperature and measured shear stress was shown during single yarn pull-out tests. Furthermore, the water treatment of pull-out samples strengthened the influence for the glass-transition temperature during the adhesion test. No influence of the surface energy of the used polymer impregnation for carbon fibres on the pull-out test was detected.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.