A B S T R A C TCarbon fibers have been processed from gel spun polyacrylonitrile copolymer on a continuous carbonization line at Georgia Tech (GT) with a tensile strength in the range of 5.5-5.8 GPa, and tensile modulus in the range of 354-375 GPa. This combination of strength and modulus is the highest for any continuous fiber reported to date, and the gel spinning route provides a pathway for further improvements in strength and modulus for mass production of carbon fibers. At short gauge length, fiber tensile strength was as high as 12.1 GPa, which is the highest value ever reported for a PAN based carbon fiber. Structure analysis shows random flaws of about 2 nm size, which results in limiting tensile strength of higher than 20 GPa. Inter-planar turbostratic graphite shear modulus in high strength carbon fibers is 30 GPa, while in graphite the corresponding value is only 4 GPa.
A novel method to perform nanoscale mechanical characterization of highly deformable nanofibers has been developed. A microelectromechanical system ͑MEMS͒ test platform with an on-chip leaf-spring load cell that was tuned with the aid of a focused ion beam was built for fiber gripping and force measurement and it was actuated with an external piezoelectric transducer. Submicron scale tensile tests were performed in ambient conditions under an optical microscope. Engineering stresses and strains were obtained directly from images of the MEMS platform, by extracting the relative rigid body displacements of the device components by digital image correlation. The accuracy in determining displacements by this optical method was shown to be better than 50 nm. In the application of this method, the mechanical behavior of electrospun polyacrylonitrite nanofibers with diameters ranging from 300 to 600 nm was investigated. The stress-strain curves demonstrated an apparent elastic-perfectly plastic behavior with elastic modulus of 7.6± 1.5 GPa and large irreversible strains that exceeded 220%. The large fiber stretch ratios were the result of a cascade of periodic necks that formed during cold drawing of the nanofibers.
ABSTRACT-An apparatus has been designed and implemented to measure the elastic tensile properties (Young's modulus and tensile strength) of surface micromachined polysilicon specimens. The tensile specimens are "dog-bone" shaped ending in a large "paddle" for convenient electrostatic or, in the improved apparatus, ultraviolet (UV) light curable adhesive gripping deposited with electrostatically controlled manipulation. The typical test section of the specimens is 400 µm long with 2 µm × 50 µm cross section. The new device supports a nanomechanics method developed in our laboratory to acquire surface topologies of deforming specimens by means of Atomic Force Microscopy (AFM) to determine (fields of) strains via Digital Image Correlation (DIC). With this tool, high strength or non-linearly behaving materials can be tested under different environmental conditions by measuring the strains directly on the surface of the film with nanometer resolution.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.