The aim of this study was to evaluate the correlation between the percent of inorganic filler by weight (wt. %) and by volume (vol. %) of 11 flowable resin composites (FRCs) and their mechanical properties. To establish the correlation, the quantity of inorganic filler was determined by combustion and shape/size analyzed by SEM images. The compressive strength (CS), flexural strength (FS), and flexural modulus (FM) were determined. The CS values were between 182.87-310.38 MPa, the FS values ranged between 59.59 and 96.95 MPa, and the FM values were between 2.34 and 6.23 GPa. The percentage of inorganic filler registered values situated between 52.25 and 69.64 wt. % and 35.35 and 53.50 vol. %. There was a very good correlation between CS, FS, and FM vs. the inorganic filler by wt. % and vol. %. (R2 = 0.8899–0.9483). The highest regression was obtained for the FM values vs. vol. %. SEM images of the tested FRCs showed hybrid inorganic filler for Filtek Supreme XT (A3) and StarFlow (A2) and a homogeneous type of inorganic filler for the other investigated materials. All of the FS values were above 50 MPa, the ISO 4049/2019 limit for FRCs.
The aim of this research was to develop new electrospun membranes (EMs) based on polycaprolactone (PCL) with or without metronidazole (MET)/nano-hydroxyapatite (nHAP) content. New nHAP with a mean diameter of 34 nm in length was synthesized. X-ray diffraction (XRD) and attenuated total reflectance Fourier transform infrared spectroscopy (FTIR-ATR) were used for structural characterization of precursors and EMs. The highest mechanical properties (the force at maximum load, Young’s modulus and tensile strength) were found for the PCL membranes, and these properties decreased for the other samples in the following order: 95% PCL + 5% nHAP > 80% PCL + 20% MET > 75% PCL + 5% nHAP + 20% MET. The stiffness increased with the addition of 5 wt.% nHAP. The SEM images of EMs showed randomly oriented bead-free fibers that generated a porous structure with interconnected macropores. The fiber diameter showed values between 2 and 16 µm. The fiber diameter increased with the addition of nHAP filler and decreased when MET was added. New EMs with nHAP and MET could be promising materials for guided bone regeneration or tissue engineering.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.