The evaluations of the fibers characteristics, bioactivity, pre-osteoblastic cell responses, and osteoconductivity of the non-woven SiO(2)-CaO gel fabric made by electrospinning method was carried out. Silica gels with four different calcium contents were prepared by condensation following hydrolysis of tetraethyl orthosilicate under acidic conditions. The molar ratios of Ca to Si prepared ranged from 0 to 0.15. SiO(2)-CaO gel fabrics were heat-treated at 300 degrees C for 3 h after spinning under an electric field of 2 kV/cm. As the Ca to Si ratio increased, the diameter of electrospun SiO(2)-CaO gel fibers increased because the viscosity of the SiO(2)-CaO gel solution increased. The apatite-forming ability of heat-treated, non-woven SiO(2)-CaO gel fabric was evaluated in simulated body fluid and tended to increase with an increasing Ca to Si molar ratio. However, proliferation and differentiation tended to decrease with an increasing Ca to Si molar ratio. The sample which had the Ca to Si ratio as 0.10 showed good osteoconductivity in vivo in the calvarial defect New Zealand white rabbit model compared to that had the Ca to Si ratio as 0 and empty defect. These results strongly suggest that non-woven SiO(2)-CaO gel fabric made by the electrospinning method has potential for application as a bone grafting material.
This article describes a novel method for the preparation of a biodegradable non-woven poly(ε-caprolactone) fabric with a partially embedded apatite surface designed for application as a scaffold material for bone tissue engineering. The non-woven poly(ε-caprolactone) fabric was generated by the electro-spinning technique and then apatite was coated in simulated body fluid after coating the PVA solution containing CaCl ·2H O. The apatite crystals were partially embedded or fully embedded into the thermoplastic poly(ε-caprolactone) fibers by controlling the degree of poly(ε-caprolactone) fiber surface melting in a convection oven. Identical apatite-coated poly(ε-caprolactone) fabric that did not undergo heat-treatment was used as a control. The features of the embedded apatite crystals were evaluated by FE-SEM, AFM, EDS, and XRD. The adhesion strengths of the coated apatite layers and the tensile strengths of the apatite coated fabrics with and without heat-treatment were assessed by the tape-test and a universal testing machine, respectively. The degree of water absorbance was assessed by adding a DMEM droplet onto the fabrics. Moreover, cell penetrability was assessed by seeding preosteoblastic MC3T3-E1 cells onto the fabrics and observing the degrees of cell penetration after 1 and 4 weeks by staining nuclei with DAPI. The non-woven poly(ε-caprolactone) fabric with a partially embedded apatite surface showed good water absorbance, cell penetrability, higher apatite adhesion strength, and higher tensile strength compared with the control fabric. These results show that the non-woven poly(ε-caprolactone) fabric with a partially embedded apatite surface is a potential candidate scaffold for bone tissue engineering due to its strong apatite adhesion strength and excellent cell penetrability. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 105A: 1973-1983, 2017.
Poly(lactic-co-glycolic)acid and silica gel fibers mixed non-woven fabric was made by electro-spinning method for the potential application as a bone grafting material. The silica gel, the source material for electro-spinning, was prepared by the hydrolysis of tetraethyl orthosilicate in the presence of calcium salt, water, hydrochloric acid and ethanol. Poly(lactic-co-glycolic)acid solution was prepared by dissolving it in the hexafluoroisopropanol. Then, they were transferred to two separate syringes which were connected to the high voltage supply generating a high electric field between the spinneret and the ground collecting drum. The silica gel containing calcium and poly(lactic-co-glycolic)acid solution were spun together under the electric field of 2 ㎸/㎝. The FE-SEM observations showed that the silica gel and poly(lactic-co-glycolic)acid fibers were mixed together completely and its handling property was much improved compared to that of the non-woven silica gel fabric. After soaking in the SBF for 1 week, low crystalline apatite crystals were also observed to occur on the silica fiber surfaces first and then they were also observed to occur on the poly(lactic-co-glycolic)acid fiber surfaces. From the results, it can be concluded that the poly(lactic-co-glycolic)acid and silica gel fibers mixed non-woven fabric made by electro-spinning method has a bioactivity. It means it has a potential to be used as a bone grafting material because of its apatite-forming ability, high surface area to volume ratio and high porosity.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.