The marginal and internal fit of both PEKK and zirconia copings of both canine and molar were within the clinically acceptable range. However, the PEKK presented better fitness compared with the zirconia.
Background/purpose
To evaluate the reproducibility of the marginal and internal gaps of metal copings fabricated using dental micro-stereolithography (μ-SLA), which is an additive manufacturing system.
Materials and methods
A study cast of abutment tooth 46 was made from type-IV dental stone and was scanned to create a standard triangulation language file. Arrays of one (ORM), three (TRM), and six (SRM) resin copings were then fabricated on the μ-SLA build platform using investment, burnout, and casting (
n
= 12). The marginal and internal gaps of these metal copings were measured using a silicone-replica technique with a digital microscope (×160). The data obtained were analyzed using a non-parametric Kruskal–Wallis H test, a post-hoc Mann–Whitney U test, and a Bonferroni correction.
Results
The mean and standard deviation of the marginal gap for each group were measured and found to be 81.1 and 53.2 μm, 68.3 and 44.8 μm, and 90.3 and 57.7 μm for ORM, TRM, and SRM, respectively. There were no statistical differences in the marginal gaps of the three groups (
p
> 0.05).
Conclusion
The marginal and internal gap of ORM, TRM and SRM groups were considered clinically acceptable.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.