Gold-free Ta/Al-based ohmic contacts fabricated by sputtering on AlGaN/GaN heterostructures and annealed at low temperature were investigated. The presence of a thin AlN spacer layer at the AlGaN/GaN heterojunction is demonstrated to prevent the ohmic contact formation as shown by rectifying behavior after annealing. Ta as an additional capping layer on Al leads to a severe morphology degradation and subsequent deterioration of the metal stack after annealing at 600 • C due to strong Ta-Al alloying verified by transmission electron microscopy. Using the compound metal TiN as capping layer circumvents the alloy formation, thereby making the contacts much more stable under annealing. A low contact resistance of 0.8 Ω mm was obtained using Ta/Al/TiN metal layers annealed at only 500 • C. The nature of the current transport was investigated by analyzing the temperature dependence of the specific contact resistance, which points towards a current path through the AlGaN barrier by thermionic field emission.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.