We investigated the short-term (4 weeks)color stability of light-cure and dual-cure resin cements. Sixty disk-shaped test specimens of adhesive resin cement (10 × 1 mm) were prepared. One feldspathic porcelain test specimen (12 × 14 × 0.8 mm) was prepared from a prefabricated ceramic block. The feldspathic sample was placed on the resin cement disk and all the measurements were performed without cementation. Specific color coordinate differences (ΔL, Δa, and Δb), and the total color differences (ΔE) were calculated after immersion in distilled water for different periods. Data were compared using one-way analysis of variance (
Background: This in vitro study aimed to evaluate the amount of polymerizing light passing through hybrid ceramic specimens in different shades and thicknesses. Methods: Rectangular-shaped feldspathic ceramic computer aided design and computer aided manufacturing (CAD-CAM) blocks and translucent and high translucent polymer infiltrated hybrid ceramic CAD-CAM blocks in four different shades (1M1, 1M2, 2M2, and 3M2) were sectioned in four different thicknesses (0.8, 1.5, 2, and 3 mm), and a total of 48 groups (n = 10) were obtained. Feldspathic ceramic specimens served as the control group. The light transmission of each ceramic specimen was measured three times by using a light-emitting diode and a radiometer. Data were statistically analyzed by using univariate analysis of variance (ANOVA) followed by one-way ANOVA, Tukey honest significant difference, and Tamhane T2 tests (α = 0.05). Results: Translucent polymer infiltrated hybrid ceramic specimens exhibited significantly (p < 0.001) lower light transmission values than high translucent polymer infiltrated hybrid ceramic and feldspathic ceramic specimens, whereas feldspathic ceramic specimens exhibited significantly (p < 0.001) higher light transmission than translucent and high translucent polymer infiltrated hybrid ceramic specimens. The amount of light transmission significantly (p < 0.05) decreased when the shade value decreased and the thickness increased. Conclusions: Polymer infiltrated hybrid ceramic specimens showed lower light transmission values than feldspathic ceramic specimens, and the amount of light transmission was affected by the ceramic shade and thickness.
BackgroundThe aim of the present study was to determine the effect of different surface treatments on light transmission of aesthetic feldspathic ceramics used in CAD-CAM chairside restorations.MethodsForty eight feldspatic ceramic test specimens were prepared from prefabricated CAD-CAM blocks by using a slow speed diamond saw. Test specimens were prepared and divided into 4 groups (n = 12). In the control group, no surface treatments were applied on the feldspathic ceramic surfaces. In the hydrofluoric acid group, the bonding surfaces of feldspathic ceramics were etched with 9.5 % hydrofluoric acid. In the sandblasting group the feldspathic ceramic surfaces were air-abraded with 30-μm alumium oxide (Al2O3) particles and Er:YAG laser was used to irradiate the ceramic surfaces. The incident light power given by the LED device and the transmitted light power through each ceramic sample was registered using a digital LED radiometer device. Each polymerization light had a light guide with 8-mm-diameter tips. Light transmission of feldspathic ceramic samples was determined by placing it on the radiometer and irradiating the specimen for 10 s at the highest setting for each light polymerization. All specimens were coated with gold using a sputter coater and examined under a field emission scanning electron microscope. Surface roughness measurement each group were evaluated with 3D optical surface and tactile profilometers.ResultsOne-way ANOVA test results revealed that both surface conditioning method significantly affect the light transmittance (F:412.437; p < 0.001) and the surface roughness values (F:16.386; p < 0.001). Al2O3 and Er-YAG laser application reduced the light transmission significantly (p < 0.05).ConclusionsThe laser and Al2O3 applications reduced the light transmission of 1.5 mm thickness feldspathic ceramic material below the value of 400 mW/cm2 which is critical limit for safe polymerization.
Background This in vitro study evaluated the effect of amine-free initiator system and polymerization type on long-term color change of amine-free light-cure and dual-cure resin cements. Methods Sixty disk-shaped specimens (10 × 1 mm) were prepared from six different amine-free resin cements; NX3 Nexus light-cure (LC) and dual-cure (DC), Variolink Veneer (LC) and Variolink II (DC), Relyx Veneer (LC) and Rely X Ultimate (DC). A feldspathic porcelain specimen (12 × 14 × 0.8 mm) was obtained from a CAD/CAM block (Cerec Blocks; Sirona Dental Systems GmbH, Bensheim, Germany) for color testing. The feldspathic specimen was placed on the resin cement disk and all measurements were performed without cementation. A spectrophotometer was used for color measurements. Specimens were subjected to thermal aging (5 °C and 55 °C; 5000 and 20,000 cycles). Specific color coordinate differences (ΔL, Δa, and Δb) and the total color differences (ΔE00) were calculated after immersion in distilled water for different periods. Normality of data distribution was tested by using the Kolmogorov–Smirnov test. Data were statistically in a model of repeated measures, using multivariate tests and Tukey’s multiple comparison tests at a significance level of p < 0.05. Results ∆E00 values of resin cements were influenced by cycle periods, significantly (p < 0.05). The highest ΔE00 values for long term were obtained in the NX3 (DC) (3.49 ± 0.87) and the lowest in the NX3 (LC) (1.41 ± 0.81). NX3 (LC), Variolink (DC), RELY X (LC) resin cements showed clinically acceptable color change after long-term aging (∆E00 < 1.8). Conclusion Light-cure resin cements should be preferred for long-term color stability of full ceramic restorations.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.