One of the methods used to optimize oil production is biopolymer injection. In this study, nanocellulose from cotton leaves was made into a biopolymer by combining the cotton leaf synthesis method with ascorbic acid, then sonified and hydrolyzed using ethanol. SEM and FTIR tests were carried out to see the size and chemical structure. The rheology of KLNC biopolymer was compared with the bipolymer from Xanthan Gum. The salinity and compatibility tests were carried out at various concentrations, as well as knowing the resistance of the biopolymer at reservoir temperature. The results of this study, the morphological shape of KLNC shows that the extraction process does not damage the surface structure. With the same concentration, KLNC biopolymer had a higher viscosity compared to Xanthan Gum biopolymer. KLNC biopolymer is more resistant to salinity and thermal than Xanthan Gum. So that KLNC Biopolymer has the potential to be further developed and researched.
Alquran merupakan mukjizat Nabi Muhammad Saw. yang berfungsi untuk melegitimasi kerasulannya. Akal manusia belum bisa menerima kedudukannya sebagai Rasul tanpa membawa bukti kerasulannya dari Allah yang berupa mukjizat. Karena itu, setiap Rasul mempunyai mukjizat sebagai tanda kenabian dan risalahnya. Tanpa mukjizat itu, niscaya manusia tidak akan beriman pada mereka. Meskipun tingginya akhlak Rasul maupun pentingnya pesan yang dibawanya, atau tingginya intelektualitas, atau kedudukannya, masih belum cukup untuk menyatakan kerasulannya kepada manusia. Alquran bukan buku ketuhanan, bukan pula buku hukum, melainkan buku petunjuk bagi manusia. Otentisitas Alquran dijaga oleh Allah Swt. sejak pertama diwahyukan kepada Nabi Muhammad hingga akhir zaman. Oleh karena itu, Alquran tidak mengalami penyimpangan, perubahan dan keterputusan sanad seperti terjadi pada kitab-kitab terdahulu.
[ID] Pelaksanaaan proses penyemenan yang baik pada sumur minyak merupakan aspek penting yang berpengaruh pada suskesnya produksi minyak ke permukaan. Untuk itu, penggunaan additif dalam suspense semen direkomendasikan supaya kulitas suspense semen tetap stabil selama proses penyemenan berlangsung. Melakui penelitian ini kualitas bentonite lokal dan bentonite komersial terhadap parameter compressive strength(CS) dan shear bond strength (SBS) akan dibandingkan. Pengukuran CS dan SBS dilkukan berdasarkan rekomendasi dari American Petroleum Institute (API) pada tujuh buah sampel suspense semen dengan konsentrasi aditif yang bervariasi. Hasil penelitian terhadap bentonite lokal menunjukkan penurunan nilai CS dengan bertambahnya konsentrasi aditif. Konsentrasi optimum bentonite lokal adalah 1.6% dengan nilai CS sebesar 1649 psi, 6% dibawah nilai CS untuk sampel suspense semen dan bentonite komersial pada konsentrasi yang sama. Untuk nilai SBS, konsentrasi optimum untuk aditif bentonite lokal adalah 4.8% dengan nilai SBS sebesar 439 psi, 21 % diatas nilai SBS untuk sampel semen dengan 4.8% bentonite komersial. Dari penentuan nilai CS dan SBS dapat disimpulkan bahwa penggunaan bentonite lokal dapat menjadi alternatif pengganti bentonite komersial dimana hasil pengukuran CS dan SBS tidak menunjukkan perbedaan yang signifikan.
[EN] The implementation of a good cementing process in oil wells is an important aspect that affects the success of oil production to the surface. For this reason, the use of additives in semen suspense is thought that the quality of the cement suspension remains stable during the cementing process. By doing this research, the quality of local bentonite and commercial bentonite against the parameters of compressive strength (CS) and shear bond strength (SBS) will be compared. CS and SBS measurements were carried out based on recommendations from the American Petroleum Institute (API) on seven cement suspension samples with varying additive concentrations. The results of research on local bentonite showed a decrease in the value of CS with an increase in additive concentration. The optimum concentration of local bentonite is 1.6% with a CS value of 1649 psi, 6% below the CS value for cement and commercial bentonite suspense samples at the same concentration. For the SBS value, the optimum concentration for local bentonite additives is 4.8% with an SBS value of 439 psi, 21% above the SBS value for cement samples with 4.8% commercial bentonite. From the determination of CS and SBS values, it can be shown that the use of local bentonite can be an alternative to commercial sites where the CS and SBS measurement results do not show a significant difference.
Demulsifier digunakan untuk mengatasi masalah emulsi minyak mentah pada saat produksi. Artikel ini memuat uji laboratorium demulsifier lokal dari minyak kelapa dan lemon dibandingkan demulsifier komersil. Parameter yang diperiksa adalah nilai pemisahan emulsi, pengaruh parameter pengujian terhadap pemisahan air secara statistik, dan water quality hasil demulsifikasi dengan uji TDS (Total Dissolved Solid) dan pH. Penelitian ini menggunakan metode saponifikasi dalam pembuatan demulsifier dan pengujian demulsifier menggunakan metode bottle test. Variasi temperatur adalah 400C, 500, 600C, 700C, dan 800C dengan konsentrasi 1ml, 3ml, dan 5 ml. Hasil penelitian menunjukkan bahwa demulsifier lokal mampu memecah emulsi di seluruh temperatur pengujian. Pemisahan tertinggi terjadi pada temperatur 600C,700C, dan 800C dengan konsentrasi optimal 3ml dan 5 ml dan hasil pemisahan sebesar 32 ml dan 33 ml. Di sisi lain demulsifier komersil pada temperatur 400C dan konsentrasi 5ml gagal memecah emulsi. Pengaruh temperatur dan konsentrasi terhadap pemisahan air secara berurut sebesar 42,5 % dan 2,7%. Water quality yang baik hasil demulsifikasi terjadi pada pengujian sampel demulsifier lokal 2 dengan TDS 244 ppm dan pH 6,99.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.