No abstract

In the exploratory study presented in this paper, an attempt was made to develop different mixtures of ultrahigh performance concrete (UHPC) using various locally available natural and industrial waste materials as partial replacements of silica fume and sand. Materials such as natural pozzolana (NP), fly ash (FA), limestone powder (LSP), cement kiln dust (CKD), and pulverized steel slag (PSS), all of which are abundantly available in Saudi Arabia at little or no cost, were employed in the development of the UHPC mixtures. A base mixture of UHPC without replacement of silica fume or sand was selected and a total of 24 trial mixtures of UHPC were prepared using different percentages of NP, FA, LSP, CKD, and PSS, partially replacing the silica fume and sand. Flow and 28-d compressive strength of each UHPC mixture were determined to finally select those mixtures, which satisfied the minimum flow and strength criteria of UHPC. The test results showed that the utilization of NP, FA, LSP, CKD, and PSS in production of UHPC is possible with acceptable flow and strength. A total of 10 UHPC mixtures were identified with flow and strength equal to or more than the minimum required.

Sometimes civil engineering infrastructures have been constructed in hot and cold weathering regions such as desert areas. In such situations, the concrete is not only smashed by hot and cold processes but also spoiled by shrinkage cracking. Therefore, this study intends to examine the influence of heat–cool cycles on high-strength concrete comprising various fibers, such as natural date palm, polypropylene, and steel fibers, and their different volume percentages. The most popular technique for improving the structural behavior of concrete is fiber insertion. Fibers decrease cracking occurrences, enhance early strength under impact loads, and increase a structure’s ability to absorb additional energy. The main goal is to examine the effects of three different types of fibers on regular concrete exposed to heat–cool cycles. For each type of fiber, three dosages of 0.2%, 0.6%, and 1% were used to create high-strength concrete. After 28 days of regular water curing and six months of exposure to heat-and-cold cycles, all specimens were tested. The heat–cool cycles entailed heating for two days at 60 °C in the oven and cooling for another two days at room temperature. The results of the experiment showed that fiber reinforcement in concrete improves its strength and durability. The flexural strength was substantially improved by increasing the date palm, polypropylene, and steel fibers into the high-strength concrete with and without heat–cool cycles. Adding increments of date palm, polypropylene, and steel fibers into high-strength concrete revealed a significant improvement in energy absorption capacity in both cases, i.e., with or without the implementation of heat–cool cycles. Therefore, the natural date palm fibers might be utilized to produce sustainable fibrous high-strength concrete and be applicable in severe weathering conditions.

The paper presents an experimental study on the evaluation of the compressive strength and modulus of elasticity of ultra-high performance concrete (UHPC) prepared with varying steel fibre contents, cured in water and exposed in air, and subjected to three exposure conditions (after 28 d of curing): laboratory environment, alternate heatingcooling cycles (heating at 608C for 2 d and then cooling at room temperature for 2 d), and alternate wet-dry cycles (wetting for 2 d in aggressive salt solution and then drying at 308C for 2 d). The test results indicate that: (a) although water-curing is better than exposure in air in improving the strength, the difference is not significant, particularly at a higher fibre content, (b) an increase in the fibre content can improve the strength and modulus of elasticity up to a certain extent, but beyond that an increase in the fibre content is not proportionally beneficial and (c) the effect of 6-month exposure to wet-dry and heating-cooling cycles on the strength and modulus of elasticity is negligible; indeed, the heating-cooling cycled specimens have strength and modulus of elasticity higher than the specimens not subjected to the cyclic exposures.

In this study, PET plastic waste, which is a type of polymer commonly used in the manufacture of plastic bottles, has been incorporated into concrete by partially replacing the natural fine aggregate. An experimental study was conducted by casting and testing 90 concrete cylinders and 54 concrete cubes. A concrete mixture was designed in which the natural fine aggregate was substituted partially with PET plastic waste (PW) at a ratio of 0%, 25%, and 50%, with various w/c ratios of .40, .45, and .55. Physical, mechanical, and durability properties were assessed. The downside of the test results show degradation in each of the following characteristics: slump, compressive strength, splitting tensile strength, ultrasonic pulse velocity, water absorption, and porosity. The degradation of these characteristics increased with the increase in the volume of plastic aggregate (PA) and the w/c ratio. While the positive side of the results showed that with the increase of the PA volume and the w/c ratio, the fresh and dry densities decreased further, and by using 50% PET, the dry density became below 2000 kg/m3. Therefore, it is classified as lightweight concrete. Moreover, the fracture of concrete changed from brittle to more ductile compared to control concrete. Also, the thermal conductivity decreased significantly (11%–47%), and by using 50% of PET, the thermal conductivity became less than .71 W/mK, and accordingly, classified as a bearing insulator.

No abstract

No abstract

No abstract