In this study, oxide materials La1−xCaxScO3−α (x = 0.03, 0.05 and 0.10) were synthesized by the citric-nitrate combustion method. Single-phase solid solutions were obtained in the case of calcium content x = 0.03 and 0.05, whereas a calcium-enriched impurity phase was found at x = 0.10. Water uptake and release were studied by means of thermogravimetric analysis, thermodesorption spectroscopy and dilatometry. It was shown that lower calcium content in the main phase leads to a decrease in the water uptake. Conductivity was measured by four-probe direct current (DC) and two-probe ascension current (AC) methods at different temperatures, pO2 and pH2O. The effects of phase composition, microstructure and defect structure on electrical conductivity, as well as correlation between conductivity and water uptake experiments, were discussed. The contribution of ionic conductivity of La1−xCaxScO3−α rises with decreasing temperature and increasing humidity. The domination of proton conductivity at temperatures below 500 °C under oxidizing and reducing atmospheres is exhibited. Water uptake and release as well as transport properties of La1−xCaxScO3−α are compared with the properties of similar proton electrolytes, La1−xSrxScO3−α, and the possible reasons for their differences were discussed.
Investigations of phase transitions in barium cerate are carried out by methods of dilatometry and differential scanning calorimetry. Thermal desorption of gases and temperature dependences of electroconduction in dry and humid air are studied. Barium cerate exhibits complex polymorphism, undergoing a number of structural conversions at 300-1300 K. The peaks in the spectra of thermal desorption of ëé 2 and ç 2 é correlate with variations in the crystal lattice. Structural changes in BaCeO 3 affect activation energies for the carrier transport and the shares of partial conductivities.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.