In the present work, ternary SnS x Se (2−x) structures were synthesized as thin films by the spray pyrolysis technique. Structural, electrical and optical properties were studied as a function of the deposition temperature. XRD and EDS results showed the presence of the SnS x Se (2−x) phase in the films deposited at temperatures from 300 to 400 °C. The phase SnSSe was obtained at 400 °C and at higher deposition temperatures a mixture of the SnS x Se (2−x) and SnS x Se (1−x) phases becomes present in the samples. XRD also indicated a preferential growth along the (001) direction, and this result is corroborated with SEM images where nanometric flakes with the hexagonal form corresponding to the SnS x Se (2−x) phase were observed. An n-type conductivity was obtained by both Hall-Van der Pauw and Seebeck measurements in the films deposited from 300 to 400 °C. For films deposited at temperatures above 400 °C, a p-type conductivity was obtained in some samples. A Seebeck coefficient as high as 603 μV/K was obtained for the sample deposited at 400 °C. Bandgap energies were obtained from the transmittance and reflectance spectra. The bandgap varied from 2.44 to 1.04 eV, yielding a value of 1.28 eV for the SnSSe sample.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.