The Ti implants with XPEED(®) surfaces significantly enhanced apatite formation, removal torque value, and the BIC%. The Ti implants with XPEED(®) surfaces may induce strong bone integration by improving osseointegration of grit-blasted Ti implants in areas of poor quality bone.

PURPOSEThis study aimed to evaluate the effect of implant thread depth on primary stability in low density bone.MATERIALS AND METHODSThe insertion torque was measured by inserting Ti implants with different thread depths into solid rigid polyurethane blocks (Sawbones) with three different bone densities (0.16 g/cm3, 0.24 g/cm3, and 0.32 g/cm3). The insertion torque value was evaluated with a surgical engine. The static compressive strength was measured with a universal testing machine (UTM) and the Ti implants were aligned at 30° against the loading direction of the UTM. After the static compressive strength test, the Ti implants were analyzed with a Measurescope.RESULTSThe Ti implants with deeper thread depth showed statistically higher mean insertion torque values (P<.001). Groups A and group B had similar maximum static compressive strengths, as did groups C and D (P>.05). After the static compressive strength, the thread shape of the Ti implants with deeper thread depth did not show any breakage but did show deformation of the implant body and abutment.CONCLUSIONThe implants with deeper thread depth had higher mean insertion torque values but not lower compressive strength. The deep threads had a mechanical stability. Implants with deeper thread depth may increase the primary stability in areas of poor quality bone without decreasing mechanical strength.

BackgroundThis study was to investigate the effect of collagen grafted porous biphasic calcium phosphate (BCP) on cell attachment, proliferation, and differentiation. Porous BCP scaffolds with interconnected micropore structure were prepared with were prepared and then grafted with a collagen type I. The hydroxyapatite (HA) and β-tricalcium phosphate (TCP) ratio of the TCP scaffolds was about 60/40 and the collagen was crosslinked on the TCP scaffold surface (collagen-TCP).ResultsThe sintered BCP scaffolds showed fully interconnected micropore structures with submicron-sized grains. The collagen crosslinking in the scaffolds was conducted using the the N-(3-Dimethylaminopropyl)-N′-ethylcarbodiimide hydrochloride and N-hydroxysuccinimide (NHS) crosslinking method. The cell proliferation of collagen-BCP scaffolds showed a similar result to that of the BCP scaffolds. However, osteoblastic differentiation and cell attachment increased in the collagen-BCP scaffolds.ConclusionsCollagen-BCP scaffold improved the cell attachment ability in early phase and osteoblastic differentiation.

Background: Implant surface topography is a key element in achieving osseointegration. Nanostructured surfaces have shown promising results in accelerating and improving bone healing around dental implants. The main objective of the present clinical and histological study is to compare, at 4 and 6 weeks, (w) bone-to-implant contact in implants having either machined surface (MAC), sandblasted, large grit, acid-etched implant surface (SLA) medium roughness surface or a nanostructured calcium-incorporated surface (XPEED®). Methods: 35 mini-implants of 3.5 × 8.5 mm with three different surface treatments (XPEED® (n = 16)—SLA (n = 13)—MAC (n = 6), were placed in the posterior maxilla of 11 patients (6 females and 5 males) then, retrieved at either 4 or 6w in a randomized split-mouth study design. Results: The BIC rates measured at 4w and 6w respectively, were: 16.8% (±5.0) and 29.0% (±3.1) for MAC surface; 18.5% (±2.3) and 33.7% (±3.3) for SLA surface; 22.4% (±1.3) and 38.6% (±3.2) for XPEED® surface. In all types of investigated surfaces, the time factor appeared to significantly increase the bone to implant contact (BIC) rate (p < 0.05). XPEED® surface showed significantly higher BIC values when compared to both SLA and MAC values at 4w (p < 0.05). Also, at 6w, both roughened surfaces (SLA and XPEED®) showed significantly higher values (p < 0.05) than turned surface (MAC). Conclusions: Nanostructured Calcium titanate coating is able to enhance bone deposition around implants at early healing stages.