We studied the emission characteristics of white phosphorescent organic light-emitting diodes (PHOLEDs), which were fabricated using a two-wavelength method. To optimize emission characteristics of white PHOLEDs, white PHOLEDs with co-doping and blue/co-doping emitting layer (EML) structures were fabricated using a host-dopant system. The total thickness of light-emitting layer was 25 nm and the dopant of blue and red was FIrpic and Bt 2 Ir(acac) in UGH3, respectively. In case of co-doping structure, applying micro lens array film showed efficiency improvement from the current efficiency 78.5 cd/A and power efficiency 40.4 lm/W to the current efficiency 131.1 cd/A and power efficiency 65 lm/W and blue / co-doping structure showed efficiency improvement from the current efficiency 43.8 cd/A and power efficiency 22 lm/ W to the current efficiency 69 cd/A and power efficiency 32 lm/W.
Abstract:We studied the emission characteristics of white phosphorescent organic light-emitting diodes (PHOLEDs), which were fabricated using a two-wavelength method. The best blue emitting OLED and red emitting OLED characteristics were obtained at a concentration of 12 vol.% FIrpic and 1 vol.% Bt2Ir(acac) in UGH3, respectively. And the optimum thickness of the total emitting layer was 25 nm. To optimize emission characteristics of white PHOLEDs, white PHOLEDs with red/blue/red, blue/red, red/blue and co-doping emitting layer structures were fabricated using a host-dopant system. In case of white PHOLEDs with co-doping structure, the best efficiency was obtained at a structure UGH3: 12 vol. % FIrpic: 1 vol.% Bt2Ir(acac) (25 nm). The maximum brightness, current efficiency, power efficiency, external quantum efficiency, and CIE (x, y) coordinate were 13,430 cd/㎡, 40.5 cd/A, 25.3 lm/W, 17 % and (0.49, 0.47) at 1,000 cd/㎡, respectively.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.