We synthesized a highly crystalline DPP-based polymer, DPPBTSPE, which contained 1,2-bis(5-(thiophen-2-yl)selenophen-2-yl)ethene as a planar and rigid electron donating group. High- and low-molecular weight (MW) DPPBTSPE fractions were collected by Soxhlet extraction and were employed to investigate their unique charge transport properties in macroscopic films and single crystalline polymer nanowire (SC-PNW), respectively. The low-MW polymer could provide well-isolated and high aspect ratio SC-PNWs, in which the direction of π-π stacking was perpendicular to the wire growing axis. The field effect transistors made of SC-PNWs exhibited remarkably high carrier mobility of 24 cm(2) V(-1) s(-1). In addition, phototransistors (PTs) made of SC-PNW showed very high performance in terms of photoresponsivity (R) and photoswitching ratio (P). The average R of the SC PNW-based PTs were in the range of 160-170 A W(-1) and the maximum R was measured at 1920 A W(-1), which is almost three orders higher than that of thin film-based PT device.
New thienothiophene-flanked diketopyrrolopyrrole and thiophene-containing π-extended conjugated polymers with various branched alkyl side-chains were successfully synthesized. 2-Octyldodecyl, 2-decyltetradecyl, 2-tetradecylhexadecyl, 2-hexadecyloctadecyl, and 2-octadecyldocosyl groups were selected as the side-chain moieties and were anchored to the N-positions of the thienothiophene-flanked diketopyrrolopyrrole unit. All five polymers were found to be soluble owing to the bulkiness of the side chains. The thin-film transistor based on the 2-tetradecylhexadecyl-substituted polymer showed the highest hole mobility of 1.92 cm2 V(-1) s(-1) due to it having the smallest π-π stacking distance between the polymer chains, which was determined by grazing incidence X-ray diffraction. Bulk heterojunction polymer solar cells incorporating [6,6]-phenyl-C71-butyric acid methyl ester as the n-type molecule and the additive 1,8-diiodooctane (1 vol %) were also constructed from the synthesized polymers without thermal annealing; the device containing the 2-octyldodecyl-substituted polymer exhibited the highest power conversion efficiency of 5.8%. Although all the polymers showed similar physical properties, their device performance was clearly influenced by the sizes of the branched alkyl side-chain groups.
A novel bipolar host 9-(4-(9H-pyrido[2,3-b]indol-9-yl)phenyl)-9H-3,9'-bicarbazole (pBCb2Cz) was prepared for high efficiency blue phosphorescent organic light-emitting diodes (PhOLEDs), a high triplet energy (ET) material, employing electron-deficient α-carboline. pBCb2Cz (ET = 2.93 eV) was effective as a host material for FIrpic- and FCNIrpic-based blue PhOLEDs, and highest quantum efficiencies of 23.0 and 16.2%, respectively, were achieved.
Polyfluorene (PF)-based chiral alternating copolymers, i.e., PFPh and PFTh, were successfully synthesized to obtain high circular dichroism (CD) in pristine thin films.
Diketopyrrolopyrrole (DPP)-based conjugated polymer PDTDPPQT was synthesized and was used to perform epitaxial polymer crystal growth on removable 1,3,5-trichlorobenzene crystallite templates. A thin-film transistor (TFT) was successfully fabricated in well-grown large spherulites of PDTDPPQT. The charge carrier mobility along the radial direction of the spherulites was measured to be 5.46-12.04 cm(2) V(-1) s(-1), which is significantly higher than that in the direction perpendicular to the radial direction. The dynamic response of charge transport was also investigated by applying a pulsed bias to TFTs loaded with a resistor (∼20 MΩ). The charge-transport behaviors along the radial direction and perpendicular to the radial direction were investigated by static and dynamic experiments through a resistor-loaded (RL) inverter. The RL inverter made of PDTDPPQT-based TFT operates well, maintaining a fairly high switching voltage ratio (Vout(ON)/Vout(OFF)) at a relatively high frequency when the source-drain electrodes are aligned parallel to the radial direction.
A new bitellurophene-based π-conjugated polymer (PDPPBTe) was synthesized and its semiconducting property was utilized for detecting Br2. The PDPPBTe polymer exhibited a highly sensitive response to Br2, which was indicated by a significant variation of the drain current in thin-film transistors.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.