In the manufacturing of a 32M ferroelectric random access memory (FRAM) device on the basis of 0.25 design rule (D/R), one of the most difficult processes is to pattern a submicron capacitor module while retaining good ferroelectric properties. In this paper, we report the ferroelectric property of patterned submicron capacitor modules with a stack height of 380 nm, where the 100 nm-thick Pb(Zr, Ti)O 3 (PZT) films were prepared by the sol-gel method. After patterning, overall sidewall slope was approximately 70 • and cell-to-cell node separation was made to be 80 nm to prevent possible twin-bit failure in the device. Finally, several heat treatment conditions were investigated to retain the ferroelectric property of the patterned capacitor. It was found that rapid thermal processing (RTP) treatment yields better properties than conventional furnace annealing. This result is directly related to the near-surface chemistry of the PZT films, as confirmed by X-ray photoelectron spectroscopy (XPS) analysis. The resultant switching polarization value of the submicron capacitor was approximately 30 µC/cm 2 measured at 3 V.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.