Vinyl ester resin emulsion type sizing agent (HMSA-1) was synthesized by phase inversion emulsification method. Centrifugal sedimentation analysis, particle size analysis, Fourier transforms infrared spectroscopy (FTIR), and gel permeation chromatography were used to characterize HMSA-1 and Japanese commercial sizing agents (JSA-1 and JSA-2). Meanwhile, abrasion resistance, fluffs and breakage, stiffness, scanning electron microscope (SEM) were used to analyze the workability in later process of carbon fiber and surface morphology. The results showed that HMSA-1 could significantly improve handling characteristics of carbon fiber. SEM micrographs demonstrated that the sized carbon fiber had smooth surface. HMSA-1 had better compatibility with vinyl ester resin. The interlaminar shear strength (ILSS) of HMSA-1 sized carbon fiber/vinyl ester resin composite reached the maximum value of 45.96 MPa.

No abstract

A water‐soluble epoxy resin was synthesized by the reaction between novolac epoxy resin (F‐51) and diethanolamine. Then, the modified F‐51 was mixed with poly(alkylene glycol allyl glycidyl ether) as a film former of a sizing agent. A series of water‐soluble sizing agents for carbon fiber (CF) were prepared. The modified F‐51 was analyzed by Fourier Transform infrared spectroscopy. The surface morphology of the CF was characterized by scanning electron microscopy. The effects of the sizing agent on the handling characteristics were investigated by abrasion resistance, fluffs, and breakage and stiffness tests. The results show that the abrasion resistance of the sized CF increased by 114.5% and reached 2344 times and the mass of fabric hairiness decreased to 3.2 mg. The interlaminar shear strength (ILSS) test indicated that the interfacial adhesion of the composite could be greatly improved. The ILSS of the sized CF composite could reach a maximum value of 42.40 MPa. © 2013 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2014, 131, 39843.

The Graphene oxide (GO) sheets were used for preparing the epoxy resin Pickering emulsion. The particle size and the zeta potential of the Pickering emulsion were measured to evaluate its stability. The stable emulsion could be served as the film former of sizing agent for carbon fiber (CF). The effect of the Pickering emulsion stabilized by GO sheets on the properties of CF and the interfacial adhesion property of CF reinforced composite were investigated. Scanning electron microscopy (SEM) images showed that there existed a layer of sizing agent film with GO sheets evenly on the CF surface. Abrasion resistance and stiffness values of CF were tested and the results indicated that the sized CF conformed to the requirement of CF handleability. The interlaminar shear strength (ILSS) test indicated that the interfacial adhesion of the composite could be greatly improved. The fracture surfaces of CF composites were examined by SEM after ILSS tests. © 2015 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2015, 132, 42285.