Two-dimensional transition-metal carbide materials (termed MXene) have attracted huge attention in the field of electrochemical energy storage due to their excellent electrical conductivity, high volumetric capacity, etc. Herein, with inspiration from the interesting structure of pillared interlayered clays, we attempt to fabricate pillared TiC MXene (CTAB-Sn(IV)@TiC) via a facile liquid-phase cetyltrimethylammonium bromide (CTAB) prepillaring and Sn pillaring method. The interlayer spacing of TiC MXene can be controlled according to the size of the intercalated prepillaring agent (cationic surfactant) and can reach 2.708 nm with 177% increase compared with the original spacing of 0.977 nm, which is currently the maximum value according to our knowledge. Because of the pillar effect, the assembled LIC exhibits a superior energy density of 239.50 Wh kg based on the weight of CTAB-Sn(IV)@TiC even under higher power density of 10.8 kW kg. When CTAB-Sn(IV)@TiC anode couples with commercial AC cathode, LIC reveals higher energy density and power density compared with conventional MXene materials.

High–energy density lithium (Li) metal batteries (LMBs) are promising for energy storage applications but suffer from uncontrollable electrolyte degradation and the consequently formed unstable solid-electrolyte interphase (SEI). In this study, we designed self-assembled monolayers (SAMs) with high-density and long-range–ordered polar carboxyl groups linked to an aluminum oxide–coated separator to provide strong dipole moments, thus offering excess electrons to accelerate the degradation dynamics of carbon-fluorine bond cleavage in Li bis(trifluoromethanesulfonyl)imide. Hence, an SEI with enriched lithium fluoride (LiF) nanocrystals is generated, facilitating rapid Li + transfer and suppressing dendritic Li growth. In particular, the SAMs endow the full cells with substantially enhanced cyclability under high cathode loading, limited Li excess, and lean electrolyte conditions. As such, our work extends the long-established SAMs technology into a platform to control electrolyte degradation and SEI formation toward LMBs with ultralong life spans.

2D transition metal carbide materials called MXene have attracted significant interest in the field of electrochemical energy storage due to their high electrical conductivity and high volumetric capacity.

The lithium metal anode (LMA) is considered as a promising star for next-generation high-energy density batteries but is still hampered by the severe growth of uncontrollable lithium dendrites. Here, we design “spansules” made of NaMg(Mn)F3@C core@shell microstructures as the matrix for the LMA, which can offer a long-lasting release of functional ions into the electrolyte. By the assistance of cryogenic transmission electron microscopy, we reveal that an in situ–formed metal layer and a unique LiF-involved bilayer structure on the Li/electrolyte interface would be beneficial for effectively suppressing the growth of lithium dendrites. As a result, the spansule-modified anode affords a high Coulombic efficiency of 98% for over 1000 cycles at a current density of 2 mA cm−2, which is the most stable LMA reported so far. When coupling this anode with the Li[Ni0.8Co0.1Mn0.1]O2 cathode, the practical full cell further exhibits highly improved capacity retention after 500 cycles.