We report high-performance fully transparent thin-film transistors (TTFTs) on both rigid and flexible substrates with transfer printed aligned nanotubes as the active channel and indium-tin oxide as the source, drain, and gate electrodes. Such transistors have been fabricated through low-temperature processing, which allowed device fabrication even on flexible substrates. Transparent transistors with high effective mobilities (approximately 1300 cm(2) V(-1) s(-1)) were first demonstrated on glass substrates via engineering of the source and drain contacts, and high on/off ratio (3 x 10(4)) was achieved using electrical breakdown. In addition, flexible TTFTs with good transparency were also fabricated and successfully operated under bending up to 120 degrees . All of the devices showed good transparency (approximately 80% on average). The transparent transistors were further utilized to construct a fully transparent and flexible logic inverter on a plastic substrate and also used to control commercial GaN light-emitting diodes (LEDs) with light intensity modulation of 10(3). Our results suggest that aligned nanotubes have great potential to work as building blocks for future transparent electronics.

Optically transparent, mechanically flexible displays are attractive for next-generation visual technologies and portable electronics. In principle, organic light-emitting diodes (OLEDs) satisfy key requirements for this application-transparency, lightweight, flexibility, and low-temperature fabrication. However, to realize transparent, flexible active-matrix OLED (AMOLED) displays requires suitable thin-film transistor (TFT) drive electronics. Nanowire transistors (NWTs) are ideal candidates for this role due to their outstanding electrical characteristics, potential for compact size, fast switching, low-temperature fabrication, and transparency. Here we report the first demonstration of AMOLED displays driven exclusively by NW electronics and show that such displays can be optically transparent. The displays use pixel dimensions suitable for hand-held applications, exhibit 300 cd/m2 brightness, and are fabricated at temperatures suitable for integration on plastic substrates.

No abstract