In this work, we take previously developed gecko-foot-hair-inspired elastomer microfiber arrays with film-terminated and mushroom-shaped tips that have demonstrated enhanced adhesion with respect to unpatterned materials under dry conditions and coat them with synthetic DOPA-containing mussel-inspired polymers to enhance adhesion repeatedly in fully submerged wet environments. A new protocol for the development of this hybrid patterned, coated adhesive, which is suitable for use in contact with both wet and dry nonflat surfaces, is described. The experimental evaluation of repeatable adhesion under both wet and dry conditions for these materials is described and compared with unpatterned and/or uncoated materials. Macroscale reversible fibrillar adhesion enhancement on a nonflat, smooth glass surface when compared with unpatterned materials under fully submerged conditions is demonstrated with no suction effect.

To address the practical issues of polymer molecular weight determination, the first accurate polymer weight-average molecular weight determination method in diverse living/controlled polymerization via DOSY (diffusion-ordered NMR spectroscopy) is reported. Based on the linear correlation between the logarithm of diffusion coefficient (log D) and the molecular weights (log Mw), external calibration curves were created to give predictions of molecular weights of narrowly-dispersed polymers. This method was successfully applied to atom transfer radical polymerization (ATRP), reversible addition–fragmentation chain transfer (RAFT), and ring-opening metathesis polymerization (ROMP), with weight-average molecular weights given by this method closely correlated to those obtained from GPC measurement.

Chemical modification strategies to improve the mechanical properties of lignin-based polyurethanes are presented. We hypothesized that treatment of lignin with Lewis acids would increase the concentration of hydroxyl groups available to react with diisocyanate monomers. Under the conditions used, hydrogen bromide-catalyzed modification resulted in a 28% increase in hydroxyl group content. Associated increases in hydrophilicity of solvent-cast thin films were also recorded as evidenced by decreases in water contact angle. Polyurethanes were then prepared by first preparing a prepolymer based on mixtures of toluene-2,4-diisocyanate (TDI) and unmodified or modified lignin, then polymerization was completed through addition of polyethylene glycol (PEG), resulting in mass ratios of TDI:lignin:PEG of 43:17:40 in the compositions investigated here. The mixture of TDI and unmodified lignin resulted in a lignin powder at the bottom of the liquid, suggesting it did not react directly with TDI. However, a homogeneous solution resulted when TDI and the hydrogen bromide-treated lignin were mixed, suggesting demethylation indeed increased reactivity and resulted in better integration of lignin into the urethane network. Significant improvements in mechanical properties of modified lignin polyurethanes were observed, with a 6.5-fold increase in modulus, which were attributed to better integration of the modified lignin into the covalent polymer network due to the higher concentration of hydroxyl groups. This research indicates that chemical modification strategies can lead to significant improvements in the properties of lignin-based polymeric materials using a higher fraction of an inexpensive lignin monomer from renewable resources and a lower fraction an expensive, petroleum-derived isocyanate monomer to achieve the required material properties.

No abstract

A new three-component bio-inspired adhesive was synthesized that is a terpolymer composed of a water-soluble segment, an interfacial adhesion segment, and a cross-linking segment. Strong wet adhesion properties are obtained utilizing a 3,4-dihydroxy-L-phenylalanine (DOPA) moiety. Poly(acrylic acid) provides high water solubility due to strong ionic interactions with water. An acrylic acid N-hydroxysuccinimide ester (NHS) was included in the adhesive polymer to allow rapid cross-linking with thiolterminated, 3-armed poly(ethylene glycol) cross-linking agents. The thiol terminal poly(ethylene glycol) was designed to be bulky to avoid possible penetration of molecules to the cell and tissue. The NHS and thiol groups react within 30 s to form covalent bonds. This design allows for rapid optimization of properties for specific applications. Lap shear strength tests on wet porcine skin demonstrated a 190% increased value in adhesion strength for adhesives having the DOPA moiety. After cross-linking, adhesion was enhanced by 450% over poly(acrylic acid-co-acrylic acid NHS) and was 240% higher than un-cross-linked poly(acrylic acid-coacrylic acid NHS-co-N-methacryloyl-3,4-dihydroxyl-L-phenylalanine). Rheology studies show adhesive viscosity drops significantly at high shear rates, demonstrating its potential to be injected via syringe. The cross-linked adhesive displayed much stronger mechanical properties and higher elastic and viscous moduli than an un-cross-linked adhesive model. Furthermore, the cross-linked adhesive has enhanced moduli near body temperature (38 °C) as compared to room temperature (23 °C), increasing the applications as a biomedical adhesive.