Spiropyran-containing stimuli-chromic flexible latex nanoparticles were synthesized for development of high-security anticounterfeiting inks with application in print-marking and finger-printing on cellulosic substrates.
Light-induced morphology transition of the functionalized spherical nanoparticles to anisotropic structures was achieved by dimerization of the surface coumarin molecules, which resulted in decreasing fluorescence intensities of coumarin moieties.
Colloidal materials have widely been used to develop innovative anticounterfeiting nanoinks for information encryption. Latex nanoparticles based on methyl methacrylate (MMA) and 2-hydroxyethyl methacrylate (HEMA) bearing hydroxyl functional groups were synthesized via semicontinuous miniemulsion polymerization. The size determination of the nanoparticles and microscopic results showed mostly spherical nanoparticles with a narrow size distribution and a mean size of about 80 nm. Two oxazolidine derivatives were physically doped at the surface of the nanoparticles to prepare photoluminescent polymer nanoparticles. Hydroxyl functional groups at the surface of the nanoparticles led to their hydrogen bonding interactions with the doped luminescent compounds. Optical analysis of the photoluminescent nanoparticles displayed different fluorescence emission and UV−vis absorbance intensities based on the amount of polar groups located at the surface of colloidal nanoparticles. Reducing the particle size to below 100 nm along with increasing the surface area can assist the decrease of the light reflectance and improvement of the latex nanoparticles' efficiency in the anticounterfeiting industry. This preparation methodology can efficiently provide remarkable photoreversible anticounterfeiting nanoinks used in different applications, such as print marking, security encoded tags, labeling, probing, and handwriting.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.