Polytetrafluoroethylene (PTFE) is a self-lubricating matrix material with low friction coefficient and corrosion resistance but high wear rate. Ceramic particle fillers could effectively improve the tribological properties of PTFE-based composites, reduce its wear rate. However, there has been much debate about anti-wear mechanisms for particle fillers, which mainly focus on wear resistance micromechanism and mechanochemistry approach. In this paper, four kinds of PTFE-based composites filled with micrometer-sized ceramic particles (SiC, Si 3 N 4 , SiO 2 and h-BN) were prepared and tested to explore their tribology properties using a pin-on-disk tribometer. The filler proportions ranged from 5 to 20 wt% in 5 wt% increments were added. The worn surfaces of the composites and transfer films attached on the steel disk were examined by Scanning electron microscopy (SEM), energydispersive x-ray spectroscopy (EDS), Fourier-transform infrared (FTIR) and 3D topographies. Ultralow wear was observed on the PTFE/SiO 2 and PTFE/Si 3 N 4 composites in wear tests, which was attributed to tribochemistry. There were protection films formed on the worn surface, which hindered further transfer of the composites. Meanwhile, adhesion of the transfer film was enhanced by metalchelate salts of perfluorinated carboxylic acids formed by tribo-chemical reactions. The wear rate of PTFE decreased by three orders of magnitude (from 6.25 * 10 −4 to 2.21 * 10 −7 mm 3 /(Nm)) after addition of 20 wt% SiO 2 particles. No chemical reaction was observed on the worn surface of PTFE/ SiC and PTFE/h-BN composites.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.