IntroductionDental ceramics are appreciated as highly esthetic restorative materials that can simulate the appearance of natural dentition better than other materials. The aim of this study was to evaluate the effect of hydrofluoric acid concentration and etching time on micro-shear bond strength (μSBS) to IPS e.max CAD and Vita Mark II of a dual cured resin cement (Panavia F2.0).MethodsThis study was an experimental in vitro study, performed in the dental material research center of Babol University of Medical Sciences in 2016. Two hydrofluoric acid concentrations (5% and 10%) and three different etching times (20, 60 and 120 seconds) were used to etch the specimens respectively. A silane coupling agent (Clearfil porcelain activator) and priming and bonding agent (Clearfil SE bond) were used on the etched surfaces in accordance to the manufacturer’s instructions of use. Then resin cement was applied on the prepared ceramic surfaces and light cured. μSBS between resin cement and the porcelains were measured with a universal testing machine. Mode of failure was observed with 40× magnification by means of a Stereo microscope. Data were analyzed with ANOVA and independent-samples t-test and Chi-square tests.ResultsIn both e.max and Vita Mark II groups, μSBS were not significantly different when different etching times (one-way ANOVA) and HF acid concentrations (Independent-samples t-test) were used (p>0.05), but the highest μSBS was shown in e.max specimens etched 60 s with 5% HF and Vita Mark II specimens etched 20 s with 10% HF. μSBS of e.max was significantly higher than Vita Mark II (p=0.00).ConclusionBest surface treatment for e.max and Vita Mark II ceramics is 20 s etch using 5 % hydrofluoric acid.
ObjectivesThe aim of this in vitro study was to evaluate the effects of the thickness and shade of 3 types of computer-aided design/computer-aided manufacturing (CAD/CAM) materials.Materials and MethodsA total of 120 specimens of 2 shades (A1 and A3) and 2 thicknesses (1 and 2 mm) were fabricated using VITA Mark II (VM; VITA Zahnfabrik), IPS e.max CAD (IE; IvoclarVivadent), and VITA Suprinity (VS; VITA Zahnfabrik) (n = 10 per subgroup). The amount of light transmission through the ceramic specimens was measured by a radiometer (Optilux, Kerr). Light-cured resin cement samples (Choice 2, Bisco) were fabricated in a Teflon mold and activated through the various ceramics with different shades and thicknesses using an LED unit (Bluephase, IvoclarVivadent). In the control group, the resin cement sample was directly light-cured without any ceramic. Vickers microhardness indentations were made on the resin surfaces (KoopaPazhoohesh) after 24 hours of dark storage in a 37°C incubator. Data were analyzed using analysis of variance followed by the Tukey post hoc test (α = 0.05).ResultsCeramic thickness and shade had significant effects on light transmission and the microhardness of all specimens (p < 0.05). The mean values of light transmittance and microhardness of the resin cement in the VM group were significantly higher than those observed in the IE and VS groups. The lowest microhardness was observed in the VS group, due to the lowest level of light transmission (p < 0.05).ConclusionGreater thickness and darker shades of the 3 types of CAD/CAM ceramics significantly decreased the microhardness of the underlying resin cement.
The effect of bleaching on the microhardness of restorative materials is material dependent. Before the application of bleaching systems on the glass ionomer materials, the application of a protective barrier should be considered.
Objectives:Iron and multivitamin drops are being frequently prescribed in children less than 2 years of age. Due to their low pH levels, these drops may lead to the softening of enamel and accelerate the destructive process. The aim of the present study was to investigate the enamel microhardness of primary teeth after exposing them to iron and multivitamin drops.Materials and Methods:Forty healthy anterior teeth were randomly divided into four groups of 10 samples each. Samples were exposed to two iron drops of Kharazmi (Iran) and Ironorm (UK) and two multivitamin drops of Shahdarou (Iran) and Eurovit (Germany) for 5 min. The surface microhardness was measured before and after exposure and data processing was done using statistical paired t-test and analysis of variance (ANOVA) test. The surface structure of the teeth was examined by scanning electron microscope (SEM).Results:In all groups, microhardness was decreased, but it was not significant in Eurovit multivitamin group (P = 0.088). The reduction rate in Kharazmi iron group was significant compared to that in other groups (P < 0.005). Hardness reduction percent for Kharazmi iron drop was 28/12 ± 47/43. In SEM analysis, irregular granular appearance was observed in the enamel exposed to Kharazmi iron drop.Conclusion:The results showed that all the studied drugs have the potential to cause erosion; this potential is the most in Kharazmi iron drop and the least in Eurovit multivitamin drops. Therefore, after using these kinds of drops, preventive measures should be used in children.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.