This study discusses the crystal structure and magnetic properties of the rare-earth doped La 0.8 R 0.2 (Fe 0.88 Si 0.12) 13 (with R = Sm, Tb) compounds. All the samples were prepared by using arc-melting technique in argon atmosphere and the obtained result shows that after heat treatment, the samples exhibited the NaZn 13-type cubic phase with a small amount of a secondary ¡-Fe phase. The magnetic properties and magnetic entropy change were determined by mean of the temperature and field dependence magnetizations. Besides the decrease in the lattice constants, there was also observed a significant increase of Curie temperature and magnetic entropy change ¹¦S M which reached a maximum of 4.5 J/kg K for La 0.8 Sm 0.2 (Fe 0.88 Si 0.12) 13 , corresponding to a relative cooling powers (RCP) of 102 J/kg for the sample.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.