Two series of thiol-modified poly(ethoxyethyl glycidyl ether) with different chain-end groups and molecular weights (PT-PEEGE-SH and Bu-PEEGE-SH), which undergo lower critical solution temperature (LCST)-type phase separation in an aqueous milieu, are grafted onto gold substrates through Au-S bonding. The water wettability of the resultant polymer-tethered surface discontinuously varies with temperature, and this alteration of wettability is reversible according to the variation in temperature of the environment. For all the polymers examined, the transition temperature on surface, TC(surf), the temperature at which half the discontinuous change in surface wettability occurs, increases with the number-average molecular weight (M(n)). This tendency does not necessarily agree with the relationship between M(n) and Tc(soln), the phase separation temperature in solution, thereby suggesting that the different factors contribute toward the determination of the Tc(surf) and Tc(soln) values. For both series of thermoresponsive polymers, the increase in crowding of the polymer chains at the surface causes the value of Tc(surf) to increase due to an increase in the interchain interaction in the outermost region of the tethered polymer chains and reduction in the chain mobility. The greater interactions between neighboring chains at the surface explain the larger dependency of Tc(surf) on M(n) as compared to that of Tc(soln).
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
customersupport@researchsolutions.com
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.