To elucidate the biochemical mechanism of osteogenesis, the effect of matrix geometry upon the osteogenesis induced by bone morphogenetic protein (BMP) was studied. A series of five porous hydroxyapatites with different pore sizes, 106-212, 212-300, 300-400, 400-500, and 500-600 microns, was prepared. A block (approximately 5 x 5 x 1 mm, 40.0 mg) of each hydroxyapatite ceramics was combined with 4 micrograms of recombinant human BMP-2 and implanted subcutaneously into the back skin of rat. Osteoinductive ability of each implant was estimated by quantifying osteocalcin content and alkaline phosphatase activity in the implant up to 4 wk after implantation. In the ceramics of 106-212 microns, the highest alkaline phosphatase activity was found 2 wk after implantation, and the highest osteocalcin content 4 wk after implantation, consistent with the results observed with particulate porous hydroxyapatite [Kuboki, Y. et al. (1995) Connect. Tissue Res. 32: 219-226]. Comparison of the alkaline phosphatase activities at 2 wk and the osteocalcin contents at 4 wk after implantation revealed that the highest amount of bone was produced in the ceramics implants with pore size of 300-400 microns. In the ceramics with smaller or larger pore sizes, the amount of bone formation decreased as the pore size deviated from 300-400 microns. The results indicated that the optimal pore size for attachment, differentiation and growth of osteoblasts and vascularization is approximately 300-400 microns. This study using chemically identical but geometrically different cell substrata is the first demonstration that a matrix with a certain geometrical size is most favorable for cell differentiation.
Bone morphogenetic protein (BMP) is known to require a suitable carrier to induce ectopic bone formation in vivo. Hydroxyapatite ceramics have been reported to be effective in some forms but ineffective in others as a carrier of BMP-induced bone formation. In this study we compare three geometrically different forms of hydroxyapatite to examine their functions as carriers of BMP-induced bone formation. A fraction containing all the active BMPs (BMP cocktail) was partially purified from a 4M guanidine extract from bovine bone by a three-step chromatographic procedure. The BMP cocktail was combined with each of three forms of hydroxyapatite--solid particles (SPHAP), porous particles (PPHAP), and coral-replicated porous tablets (coral-HAP)--and implanted subcutaneously into rats. Both the PPHAP and coral-HAP systems induced osteogenesis 2 weeks after implantation, as evidenced by morphological and biochemical observations. Details of the osteogenetic process were followed by double-fluorescence labeling in the coral-HAP system to confirm bone formation on the surface of hydroxyapatite. However, there was no evidence of osteogenesis or chondrogenesis in the SPHAP system. The results indicate that the geometry of the interconnected porous structure in PPHAP and coral-HAP create spaces for vasculature that lead to osteogenesis while the smooth structure and close contact of particles in SPHAP inhibit vascular formation and proliferation of mesenchymal cells, preventing bone and cartilage formation. It was concluded that the geometrical structure in hydroxyapatite ceramics that induces vasculature is crucial as a carrier for BMP-induced bone formation.
A partially purified BMP preparation was combined with a fibrous glass membrane (FGM) or porous particles of hydroxyapatite (PPHAP), and then implanted subcutaneously into the backs of rats. As a control of these new carriers, a conventional carrier of insoluble bone matrix (IBM) was also used. These new geometrically different solid-state carriers induced tissues in quite different manners. FGM/BMP implants induced cartilage formation within the entire inner area of the membrane accompanied by a small amount of bone formation on the surface of the membrane. In contrast, PPHAP/BMP implants induced only bone within the pores of PPHAP without any detectable cartilage formation. Enzyme-linked immunosorbent assay revealed that the type II collagen content in FGM/BMP was six times higher than that in IBM/BMP, while there was no detectable type II collagen in PPHAP/BMP. The results were explained by the geometric properties of the two distinctive carriers.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.