The effects of simple alkyl alcohols on the radical polymerization of N‐isopropylacrylamide in toluene at low temperatures were investigated. We succeeded in the induction of syndiotactic specificity and the acceleration of polymerization reactions at the same time by adding simple alkyl alcohols such as 3‐methyl‐3‐pentanol (3Me3PenOH) to N‐isopropylacrylamide polymerizations. The dyad syndiotacticity increased with a decrease in the temperature and an increase in the bulkiness of the added alcohol and reached up to 71% at −60 °C in the presence of 3Me3PenOH. With the assistance of NMR analysis, it was revealed that the alcohol compounds played dual roles in this polymerization system; an alcohol compound coordinating to the NH proton induced syndiotactic specificity, and that hydrogen‐bonded to the CO oxygen accelerated the polymerization reaction. The effect of syndiotacticity on the properties of poly(N‐isopropylacrylamide)s was also examined in some detail. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 4450–4460, 2006

The radical polymerizations of N‐isopropylacrylamide (NIPAAm) were carried out in toluene at low temperatures in the presence of phosphoric acid esters such as trimethyl phosphate, triethyl phosphate (TEP), tri‐n‐propyl phosphate, and tri‐n‐butyl phosphate (TBP). Syndiotactically rich poly(NIPAAm)s were obtained from −60 to 0 °C, and TEP provided the highest syndiotacticity (racemo dyad = 65%) at −40 °C. On the other hand, lowering the temperature reversed the stereoselectivity of the propagation reaction so that isotactically rich poly(NIPAAm)s were obtained at −80 °C. In particular, TBP exhibited the most isotactic specificity (meso dyad = 57%). Job's plots for NIPAAm–TBP mixtures revealed that NIPAAm and TBP formed a 1:1 complex at 0 °C and a predominantly 1:2 complex at −80 °C through a hydrogen‐bonding interaction. Therefore, the stereospecificity of NIPAAm polymerization should depend on the stoichiometry of the hydrogen‐bond‐assisted complex. Thus, the mechanism for this polymerization system was discussed. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 50–62, 2005

The radical polymerization of N‐isopropylacrylamide (NIPAAm) in toluene at low temperatures was investigated in the presence of triisopropyl phosphate (TiPP). The addition of TiPP induced a syndiotactic specificity that was enhanced by the polymerization temperature being lowered, whereas atactic polymers were obtained in the absence of TiPP, regardless of the temperature. Syndiotactic‐rich poly(NIPAAm) with a racemo dyad content of 65% was obtained at −60 °C with a fourfold amount of TiPP, but almost atactic poly(NIPAAm)s were obtained by the temperature being lowered to −80 °C. This result contrasted with the result in the presence of primary alkyl phosphates, such as tri‐n‐propyl phosphate: the stereospecificity varied from syndiotactic to isotactic as the polymerization temperature was lowered. NMR analysis at −80 °C revealed that TiPP predominantly formed a 1:1 complex with NIPAAm, although primary alkyl phosphates preferentially formed a 1:2 complex with NIPAAm. Thus, it was concluded that a slight increase in the bulkiness of the added phosphates influenced the stoichiometry of the NIPAAm–phosphate complex at lower temperatures, and consequently a drastic change in the effect on the stereospecificity of NIPAAm polymerization was observed. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 3899–3908, 2005

No abstract