This study examined the effects of moisture content (MC) on the manufacture of cement-bonded particleboard (CBP) using supercritical CO 2 in the curing process. Significant correlations were found between MC and the performance of CBP: the internal bond strength, modulus of rupture, and modulus of elasticity values of CBP achieved their maximums, when the MC of boards was approximately 30%. This finding indicated that during the curing phase of manufacturing CBP, a MC of about 30%, which is nearly equal to the water-cement (w/c) ratio of about 0.34, contributes to improved mechanical properties. However, the mechanical properties decreased when the MC was below 30%, which had a negative effect on board performance, indicating that carbon dioxide could not fully react and no carbonation occurred during the curing process. Maintaining a MC of approximately 30% as an ordinary condition of the cement required in the curing of CBP could promote the reaction of carbon dioxide to form calcium carbonate (CaCO 3 ), which leads to increased final strength of CBP. Both X-ray diffractometry and thermal gravimetry observation agreed well with these results and clarified that the increase of CaCO 3 content caused by carbonation with increased MC of boards contributed to improving the mechanical properties of CBP.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.