Bismuth vanadate (BiVO4) is a promising photoelectrode material for the oxidation of water, but fundamental studies of this material are lacking. To address this, we report electrical and photoelectrochemical (PEC) properties of BiVO4 single crystals (undoped, 0.6% Mo, and 0.3% W:BiVO4) grown using the floating zone technique. We demonstrate that a small polaron hopping conduction mechanism dominates from 250 to 400 K, undergoing a transition to a variable-range hopping mechanism at lower temperatures. An anisotropy ratio of ~3 was observed along the c axis, attributed to the layered structure of BiVO4. Measurements of the ac field Hall effect yielded an electron mobility of ~0.2 cm(2) V(-1) s(-1) for Mo and W:BiVO4 at 300 K. By application of the Gärtner model, a hole diffusion length of ~100 nm was estimated. As a result of low carrier mobility, attempts to measure the dc Hall effect were unsuccessful. Analyses of the Raman spectra showed that Mo and W substituted for V and acted as donor impurities. Mott-Schottky analysis of electrodes with the (001) face exposed yielded a flat band potential of 0.03-0.08 V versus the reversible H2 electrode, while incident photon conversion efficiency tests showed that the dark coloration of the doped single crystals did not result in additional photocurrent. Comparison of these intrinsic properties to those of other metal oxides for PEC applications gives valuable insight into this material as a photoanode.

Reaching the goal of economical photoelectrochemical (PEC) water splitting will likely require the combination of efficient solar absorbers with high activity electrocatalysts for the hydrogen and oxygen evolution reactions (HER and OER). Toward this goal, we synthesized an amorphous FeOOH (a-FeOOH) phase that has not previously been studied as an OER catalyst. The a-FeOOH films show activity comparable to that of another OER cocatalyst, Co-borate (Co-Bi), in 1 M Na2CO3, reaching 10 mA/cm(2) at an overpotential of ∼550 mV for 10 nm thick films. Additionally, the a-FeOOH thin films absorb less than 3% of the solar photons (AM1.5G) with energy greater than 1.9 eV, are homogeneous over large areas, and act as a protective layer separating the solution from the solar absorber. The utility of a-FeOOH in a realistic system is tested by depositing on amorphous Si triple junction solar cells with a photovoltaic efficiency of 6.8%. The resulting a-FeOOH/a-Si devices achieve a total water splitting efficiency of 4.3% at 0 V vs RHE in a three-electrode configuration and show no decrease in efficiency over the course of 4 h.

We report that conductive single nanoparticle (NP) collisions can involve a significant component of the mass transport to the electrode of the charged NPs by migration. Previously, collision events of catalytic NPs were described as purely diffusional using random walk theory. However, the charged NP can also be attracted to the electrode by the electric field in solution (i.e., migration) thereby causing an enhancement in the collision frequency. The migration of charged NPs is affected by the supporting electrolyte concentration and the faradaic current flow. A simplified model based on the NP transference number is introduced to explain the migrational flux of the NPs. Experimental collision frequencies and the transference number model also agreed with more rigorous simulation results based on the Poisson and Nernst−Planck equations.

A new dispenser and scanner system is used to create and screen Bi-M-Cu oxide arrays for cathodic photoactivity, where M represents 1 of 22 different transition and post-transition metals. Over 3000 unique Bi : M : Cu atomic ratios are screened. Of the 22 metals tested, 10 show a M-Cu oxide with higher photoactivity than CuO and 10 show a Bi-M-Cu oxide with higher photoactivity than CuBi2O4. Cd, Zn, Sn, and Co produce the most photoactive M-Cu oxides, all showing a 200-300% improvement in photocurrent over CuO. Ag, Cd, and Zn produce the highest photoactivity Bi-M-Cu oxides with a 200-400% improvement over CuBi2O4. Most notable is a Bi-Ag-Cu oxide (Bi : Ag : Cu atomic ratio of 22 : 3 : 11) which shows 4 times higher photocurrent than CuBi2O4. This material is capable of evolving hydrogen under illumination in neutral electrolyte solutions at 0.6 V vs. RHE when Pt is added to the surface as an electrocatalyst.

We report that oxide composite electrodeposition can be used for the facile preparation of metal-doped BiVO 4 photoelectrodes for photoelectrochemical water oxidation. The photoactivity of electrodeposition film was improved by the addition of a small amount of tungstic acid particles during the electrodeposition. These particles are incorporated in the deposit and finally generate tungstendoped bismuth vanadate. The suspended particles in the plating solution were electrostatically attracted to the cathode and accordingly incorporated into the deposit (electrostatic deposition). WO 3 nanoparticles (NPs) can be used instead of tungstic acid, to yield a BiVO 4 with different properties. Enhanced photoelectrochemical (PEC) water oxidation was confirmed via scanning electrochemical microscopy (SECM) by detecting increased oxygen evolution with using optical fiber incorporating a ring electrode.