Several formulations of alternative alloys have been proposed for the substitution of gold-based alloys used in Dentistry. Recently, a Ni-Cr-Ti-based alloy has been introduced. The purpose of this work was to verify the marginal adaptation obtained with one-piece superstructures for implant-supported prostheses obtained in Ni-Cr-Ti alloy, compared to a semi-noble alloy Pd-Ag. Eight superstructures for each alloy were produced over 4 implants in the anterior region of the mandible. The superstructures were placed in a torquemeter and the fixation screw of implant #1 was tightened with a 20 Ncm load with the others loosened (Sheffield test). The unfitness (in mm) was measured using a three-dimensional optical measurer in each implant, in the buccal and lingual aspects. The obtained data were submitted to statistical analysis by the analysis of variance and Tukey's test at 5% level. Significant differences were found for the factors material (p≤0.05), with Ni-Cr-Ti pieces better than Pd-Ag ones, and implants (p≤0.01). There were no significant differences for the factor position and interactions among factors (p>0.05). Based on the analysis of the data, it is possible to conclude that the Ni-Cr-Ti alloy makes possible the obtainment of one-piece implant-supported superstructures with a smaller misfit compared to the one obtained in Pd-Ag alloy, traditionally indicated for this situation. Additional tests may verify the superiority of the Ni-CrTi alloy.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.