Summary: Lack of initial mechanical stability of cementless prostheses may be responsible for fibrous tissue fixation of prosthetic components to bone. TO study the influence of micromovements on bony ingrowth into titanium alloy (Ti) and hydroxyapatite (HA)-coated implants, a loaded unstable device producing movements of 500 pm during each gait cycle was developed. Mechanically stable implants served as controls. The implants were inserted into the weight-bearing regions of all four femoral condyles in each of seven mature dogs. Histological analysis after 4 weeks of implantation showed a fibrous tissue membrane surrounding both Ti and HA-coated implants subjected to micromovements, whereas variable amounts of bony ingrowth were obtained in mechanically stable implants. The pushout test showed that the shear strength of unstable Ti and HA implants was significantly reduced as compared with the corresponding mechanically stable implants (p < 0.01). However, shear strength values of unstable HA-coated implants were significantly greater than those of unstable 'l'i implants (p < 0.01) and comparable to those of stable Ti implants. The greatest shear strength was obtained with stable HA-coated implants, which was threefold stronger as compared with the stable Ti implants (p < 0.001). Quantitative determination of bony ingrowth agreed with the mechanical test except for the stronger anchorage of unstable HA implants as compared with unstable Ti implants, where no difference in bony ingrowth was found. Unstable HA-coated implants were surrounded by a fibrous membrane containing islands of fibrocartilage with higher collagen concentration, whereas fibrous connective tissue with lower collagen concentration was predominant around unstable Ti implants. In conclusion, micromovements between bone and implant inhibited bony ingrowth and led to the development of a fibrous membrane. The presence of iibrocartilage and a higher collagen concentration in the fibrous membrane may be responsible for the increased shear strength of unstable HA implants. Mechanically stable implants with HA coating had the strongest anchorage and the greatest amount of bony ingrowth. Key Words: Bone ingrowth-Fibrous membraneHydroxyapatite-Micromotion-Porous ingrowth-Titanium. Porous coated prostheses were designed to obtain permanent fixation by ingrowth of bone into the porous implant surface. However, recent histological analyses of cementless tibia1 components (1 1,16) and total hip replacements (10,12) retrieved 285

No abstract

Repeated non-invasive measurements were performed in dogs of trabecular bone density (TBD), low density bone area (LDBA), and high density bone area (HDBA) in chronic arthritis using quantitative computed tomography (QCT). Unilateral chronic arthritis of the knee had been induced by weekly instillation of 2 ml carragheenin into the right knee joint for 12 weeks with the left knee serving as a control. CT scanning of the distal femoral condyles was performed in 12 mature dogs with chronic arthritis. Another 6 dogs underwent a longitudinal CT study starting immediately prior to induction of arthritis. During induction of arthritis TBD decreased (P less than 0.01), LDBA increased (P less than 0.05) and HDBA decreased (P less than 0.01) in the arthritic bone. Opposite changes were found on the control side, i.e. TBD increased (P less than 0.01), LDBA decreased (P less than 0.01) and HDBA increased (P less than 0.01). The chronic arthropathic bone showed 20% lower TBD (P less than 0.0001), greater LDBA (P less than 0.0001) and lower HDBA (P less than 0.0001) as compared with the control bone. Reproducibility tests of TBD showed a coefficient of variation of 0.8%. Indentation tests and histomorphometric analyses confirmed the bone density changes as measured by CT.