SiO2 is the most widely used dielectric material but its growth or deposition involves high thermal budgets or suffers from shadowing effects. The low-temperature method presented here (150 degrees C) for the preparation of SiO2 by thermal atomic layer deposition (ALD) provides perfect uniformity and surface coverage even into nanoscale pores, which may well suit recent demands in nanoelectronics and nanotechnology. The ALD reaction based on 3-aminopropyltriethoxysilane, water, and ozone provides outstanding SiO2 quality and is free of catalysts or corrosive by-products. A variety of optical, structural, and electrical properties are investigated by means of infrared spectroscopy, UV-Vis spectroscopy, secondary ion mass spectrometry, capacitance-voltage and current-voltage measurements, electron spin resonance, Rutherford backscattering, elastic recoil detection analysis, atomic force microscopy, and variable angle spectroscopic ellipsometry. Many features, such as the optical constants (n, k) and optical transmission and surface roughness (1.5 A degrees), are found to be similar to thermal oxide quality. Rapid thermal annealing (RTA) at 1000 degrees C is demonstrated to significantly improve certain properties, in particular by reducing the etch rate in hydrofluoric acid, oxide charges, and interface defects. Besides a small amount of OH groups and a few atomic per mille of nitrogen in the oxide remaining from the growth and curable by RTA no impurities could be traced. Altogether, the data point to a first reliable low temperature ALD-growth process for silicon dioxide

Low-area density ZnO nanowire arrays, growing perpendicularly to the substrate, are synthesized with high-pressure pulsed laser deposition. The introduction of a ZnO buffer layer enables us to fabricate individual nanowires several micrometres apart (area density<0.1 nanowire microm(-2)), suppressing any shadowing effect by neighbouring nanowires during subsequent growth. These low density ZnO nanowires, whose c-axis is perpendicular to the substrate surface, are then used as templates to grow ZnO/ZnMgO core-shell nanowire heterostructures with conventional low-pressure pulsed laser deposition. Cathodoluminescence spectroscopy as well as transmission electron microscopy show that a sharp interface forms between the ZnO core and the ZnMgO shell. Based on these findings, we have grown a series of radial ZnO/ZnMgO quantum wells with different thicknesses that exhibit quantum confinement effects, with thicker quantum wells emitting at lower energies. Spatially resolved cathodoluminescence confirms the homogeneity of the quantum well structure along the full nanowire length of about 3 microm.

No abstract

No abstract

No abstract