The continuous development of constitutive equations for the finite strain deformation of glassy polymers has resulted in a number of sophisticated models that can accurately capture the materials' intrinsic behavior. Numerical simulations using these models revealed that the thermal history plays a crucial role in the macroscopic deformation. Generally, macroscopic behavior is assumed not to change during a test, however, for certain test conditions this does not hold and a relevant change in mechanical properties, known as physical aging, can be observed. To investigate the consequences of this change in material structure, the existing models are modified and enhanced by incorporating an aging term, and its parameters are determined. The result is a validated constitutive relation that is able to describe the deformation behavior of, in our case, polycarbonate over a large range of molecular weights and thermal histories, with one parameter set only.

The influence of network density on the strain hardening behaviour of amorphous polymers is studied. The network density of polystyrene is altered by blending with poly(2,6-dimethyl-1,4-phenylene-oxide) and by cross-linking during polymerisation. The network density is derived from the rubber-plateau modulus determined by dynamic mechanical thermal analysis. Subsequently uniaxial compression tests are performed to obtain the intrinsic deformation behaviour and, in particular, the strain hardening modulus. At room temperature, the strain hardening modulus proves to be proportional to the network density, irrespective of the nature of the network, i.e. physical entanglements or chemical cross-links. With increasing temperature, the strain hardening modulus is observed to decrease. This decrease appears to be related to the influence of thermal mobility of the chains, determined by the distance to the glass-transition temperature ðT 2 T g Þ: q

No abstract

No abstract