We present experimental results on the phase behavior of block copolymer/salt mixtures over a wide range of copolymer compositions, molecular weights, and salt concentrations. The experimental system comprises polystyrene- block-poly(ethylene oxide) and lithium bis(trifluoromethanesulfonyl)imide (LiTFSI) salt. It is well established that LiTFSI interacts favorably with poly(ethylene oxide) relative to polystyrene. The relationship between chain length and copolymer composition at fixed temperature is U-shaped, as seen in experiments on conventional block copolymers and as anticipated from the standard self-consistent field theory (SCFT) of block copolymer melts. The phase behavior can be explained in terms of an effective Flory-Huggins interaction parameter between the polystyrene monomers and poly(ethylene oxide) monomers complexed with the salt, χ, which increases linearly with salt concentration. The phase behavior of salt-containing block copolymers, plotted on a segregation strength versus copolymer composition plot, is similar to that of conventional (uncharged) block copolymer melts, when the parameter χ replaces χ in segregation strength.

The uncontrollable non-planar electrodeposition of lithium is a significant barrier to the widespread adoption of high energy density rechargeable batteries with a lithium metal anode. A promising approach for preventing the growth of lithium dendrites is the use of solid polymer electrolytes with a high shear modulus. Current density is the key variable in the electrodeposition of lithium. The present study is the first attempt at quantifying the effect of current density on the geometry and density of dendrites and other protrusions during electrodeposition through a solid polymer electrolyte. The geometry and density of defects formed on the lithium electrode were determined by X-ray microtomography. The tomograms revealed protrusions on the electrodeposited lithium electrodes that were either globular or dendritic, or void defects. The range of current densities over which stable, planar deposition was observed is quantified. At higher current densities, globular protrusions were observed. At the highest current density, both globular and dendritic protrusions were observed. The areal density of protrusion defects increased sharply with current density, while the overall defect density is a weak function of current density. Our work enables comparisons between the experimentally determined onset of non-planar electrodeposition and prevailing theoretical predictions with no adjustable parameters.

It is known that the addition of salts to symmetric block copolymers leads to stabilization of ordered phases and an increase in domain spacing; both trends are consistent with an increase in the effective Flory-Huggins interaction parameter between the blocks, χ. In this work, we show that the addition of salt to a disordered asymmetric block copolymer first leads to the formation of coexisting ordered phases which give way to a reentrant disordered phase at a higher salt concentration. The coexisting phases are both body centered cubic (BCC) with different domain spacings, stabilized by partitioning of the salt. Further increase in salt concentration results in yet another disorder-to-order transition; hexagonally packed cylinders are obtained in the high salt concentration limit. The coexisting phases formed at intermediate salt concentration, elucidated by electron tomography, showed the absence of macroscopic regions with distinct BCC lattices. A different asymmetric block copolymer with composition in the vicinity of the sample described above only showed only a single disorder-to-order transition. However, the dependence of domain spacing on salt concentration was distinctly non-monotonic, and similar to that of the sample with the reentrant phase behavior. This dependence appears to be an announcement of reentrant phase transitions in asymmetric block copolymer electrolytes. These results cannot be mapped on to the traditional theory of block copolymer electrolyte self-assembly based on an effective χ.