Exposing nanoscale zerovalent iron (NZVI) to dissolved sulfide species improves its performance as a remediation agent. However, the impacts of sulfur dose and sulfidation time on morphology, sulfur content, reactivity, and selectivity of the resulting sulfidized NZVI (SNZVI) have not been systematically evaluated. We synthesized SNZVI using different sulfur doses and sulfidation times and measured their properties. The measured S/Fe molar ratio in the particles ([S/Fe] particle ) was 10−500 times lower than [S/Fe] dosed but was predictable based on [S/Fe] dosed × t sulfidation . The low sulfur content (0.02−0.65 mol % S/Fe) inhibited the reaction of SNZVI with water (up to 13-fold) and increased its reactivity with trichloroethene (TCE) (up to 14-fold) and its electron efficiency (up to 20-fold). A higher [S/ Fe] particle (0.86−1.13 mol % S/Fe) led to complex particle structures and lowered the resistance to electron transfer but did not improve the benefits realized at the lower S/Fe ratios. Adding small amounts of sulfur into NZVI led to more accumulation of acetylene, especially for low Fe/TCE conditions, suggesting that sulfur lowers the rate of hydrogenation of acetylene to ethene. These results show that [S/Fe] dosed × t sulfidation can be used to predict the measured S content in the particles and that affects reactivity, longevity, and electron selectivity, for post-SNZVI.

Using the GW method within many-body perturbation theory, we investigate the quasiparticle structures of defects, including oxygen vacancy, Ti interstitial, and hydroxyl groups, in the anatase TiO2 (101) surface. We find that the deep defect state in this surface observed experimentally, which is 1 eV below the Fermi level, originates from the σ bond formed between 3d orbitals of the two under-coordinated Ti atoms at the surface oxygen vacancy. Different from the density functional theory modified with on-site Coulomb terms (DFT + U), the GW method predicts that the localized polaron in anatase (101) is a shallow defect state close to the conduction band bottom. Polaronic states play the role in pinning the Fermi level of anatase near the conduction band bottom. Our GW calculations can explain satisfactorily the coexistence of shallow and deep defect states in anatase as observed in experiments. We also find that the conduction band edge of anatase is drawn down greatly after the filling of original empty Ti 3d orbitals by excess electrons, making the calculated bandgap of the reduced anatase agree well with the experiments. This significant difference in the bandgap between the intact and the reduced anatase is missed in DFT + U.

No abstract

No abstract

No abstract

No abstract

Mechanism of water photooxidation reaction on the rutile TiO2(110) surface has been extensively discussed but still remains highly controversial. By ab initio many-body Green’s function theory, we discover a new...

A lead-free piezoelectric ceramic binary system based on bismuth sodium titanate (Bi0.5Na0.5)TiO3 (BNT)-bismuth potassium titanate (Bi0.5K0.5)TiO3 (BKT) was synthesized by conventional mixed-oxide technique. The XRD analysis showed that the rhombohedral-tetragonal morphotropic phase boundary (MPB) of the Bi0.5 (Na1-xKx)0.5 TiO3 system was in the composition range of x = 0.16 ~ 0.20. In addition, the piezoelectric properties of this system were also investigated. It was indicated that the piezoelectric properties are better with the compositions near the rhombohedral phase within the MPB than the compositions near the tetragonal phase.