No abstract

BackgroundIn this study, pyrolysis of low-density polyethylene (LDPE) and LDPE with aluminum (C/LDPE) wastes was carried out with different heating rates (5-10-20°C/min) at different temperatures (400-600-800°C). The effect of temperature and heating rate on liquid product yield was investigated. Product yields of LDPE and C/LDPE wastes were compared, and optimum liquid products were analyzed to utilize as commercial waxes for future use. MethodsTo determine the parameters of pyrolysis wastes was investigated with proximate, elemental analysis, and TGA. The as-produced liquid from pyrolysis of wastes was characterized by different characteristic tools, such as elemental analyses, GC-MS analyzes, 1 H-NMR tests, FT-IR spectra, the density, melting point, and carbon residue to compare commercial waxes. The characterization process was continued for the parameters with the optimum liquid products. ResultsAs a result of pyrolysis, the highest liquid product yield was achieved at 800°C with 5°C/min heating rate (85.87 %), and at 600°C with 5°C/min heating rate (71.3 %) for LDPE and C/LDPE, respectively. The results indicated that the derived liquid products are similar to commercial heavy wax.

No abstract

The use of latent heat storage system using phase change materials (PCM) is an efficient way of storing thermal energy. These materials store energy in the form of latent heat at constant temperature during phase transition and release the same stored energy. Paraffin is one of the important organic PCMs used with methods such as shape stabilization and encapsulation. Due to many limitations affecting the thermal performance of the material, such as the high economic cost of any technical grade paraffin, fluid leakage during the phase transition procedure, low thermal conductivity and low surface area, in order to improve the desired physical properties and thermal performance in latent heat storage, it is important to develop composite phase change materials obtained with paraffin wax. This review paper summarizes studies on phase change materials obtained using paraffin wax, and recommendations on the use of plastic, wax and nanomaterial wastes, which are excessive in the environment, in composite phase change materials are presented within the framework of global climate change mitigation strategies.

İklim değişikliğinin en önemli sebeplerinden birisi olan karbondioksit (CO2) emisyonlarının birincil kaynağı, enerji üretiminde fosil yakıtların kullanılmasıdır. Yanma sonrası oluşan CO2 emisyonlarını azaltmak için, adsorpsiyon ve özellikle karbon bazlı adsorbanların kullanımının oldukça etkili olduğu kanıtlanmıştır. Bu amaçla kullanılan karbon nanotüplerin, adsorpsiyon kapasitesini artırmak için farklı modifikasyonları kullanılmaktadır. Ancak, en uygun modifikasyon türüne karar verirken sadece adsorpsiyon kapasitesi yeterli olmamakta, pek çok teknik kriterin yanında maliyetler de gündeme gelmektedir. Bu nedenle bu çalışmada, çok duvarlı karbon nanotüplerin alternatif olarak polietilenimin (PEI), tetraetilenpentamin (TEPA), 3-aminopropiltrieoksilan (APTS) ve pürin takviyeli PEI olmak üzere dört farklı modifikasyonu ele alınmış ve en uygun modifikasyon türünü belirlemek için de çok kriterli karar verme (MCDM) teknikleri kullanılmıştır. Ele alınan kriterler (ön işlem maliyeti, modifikasyon malzemesi maliyeti, enerji ihtiyacı, adsorpsiyon kapasitesi, toplam döngü, adsorpsiyon kapasitesinin düşmesi, desorpsiyon sıcaklığı ve desorpsiyon süresi) SMART (Simple Multi-Attribute Rating Technique) ve CRITIC (Criteria Importance Through Intercritera Correlation) yöntemleri ile ağırlıklandırılmıştır. Alternatifler, her iki yöntemden elde edilen ağırlıklandırma sonuçlarıyla COPRAS (Complex Proportional Assessment) yöntemi kullanılarak karşılaştırılmıştır. Çalışma sonucunda, dört farklı karbon nanotüp modifikasyonu içinden en uygun seçeneğin pürin takviyeli PEI olduğu belirlenmiştir.