SiC/SiC continuous fiber-reinforced ceramic matrix composite (CFCC) combustor liners having protective environmental barrier coatings (EBCs) applied to the liner working surfaces have been field-tested in a Solar Turbines’ Centaur 50S SoLoNOx engine at the Chevron, Bakersfield, CA engine test site. This latest engine test ran for a total of 13,937h. The EBCs significantly increased the lifetime of the in-service liners compared with uncoated CFCC liners used in previous field-tests. The engine test was concluded when a routine borescope inspection revealed the formation of a small hole in the inner liner. Extensive microstructural evaluation of both the inner and outer liners was conducted after removal from the engine. Post-test analysis indicated that numerous degradation mechanisms contributed to the EBC and CFCC damage observed on the liners, including EBC volatilization, sub-surface CFCC oxidation and recession, and processing defects which resulted in localized EBC spallation and accelerated CFCC oxidation. The characterization results obtained from these field-tested liners have been compared with the analyses of similarly-processed CFCC/EBCs that were laboratory-tested in a high-pressure, high temperature exposure facility (the ORNL “Keiser Rig”) for >6000h.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.