The research on Characteristic of vulcanizate rubber using cassava starch composite (Manihot glaziovii) modification -latex as filler has been done. The composite variation of cassava starch concentration is 0, 40, 80, 120, 160 and 200
Since some adverse effects of using carbon black as petroleum-based filler in rubber compounding, mineral fillers may be a feasible alternative filler. This research studied the effect of the composition of pumice and clay as mineral filler in natural rubber (NR) and ethylene propylene diene monomer (EPDM) blending towards its curing characteristics and physical-mechanical properties. The effect of reinforced filled in EPDM-NR (70/30) phr blends was observed by varying 50, 70, and 90 phr of filler. While the filler was designed as the composition of pumice/clay (P/C): 20/80; 50/50; 80:20 (weight/weight). The rubber, fillers, and chemical were compounded based on ASTM D-3182. The results showed that the loading of P/C fillers in EPDM-NR blends increased scorch time and decreased cure rate index. It was found that the optimum number of filler could enhance density, modulus. Remarkably, the higher pumice composition caused the abrasion resistance and compression set improved significantly, whereas the overloading pumice and clay cause the physic-mechanical properties remained stable or evenly drop. FTIR spectra of the binary blends confirmed that the fine fillers dispersion was obtained due to some interaction bonding between silanol, aluminol of fillers with the EPDM-NR.
Industri karet remah (crumb rubber) menghasilkan limbah karet padat yang mengandung karet. Setiap pengolahan 100 kg karet Bokar menghasilkan limbah karet padat yang masih mengandung karet sekitar 3-5%. Limbah padat ini ditumpuk di pabrik dan belum sepenuhnya diproses secara efektif. Limbah padat berupa cangkang sawit mengandung silika (SiO2) yang cukup tinggi mencapai 50-56%. Cangkang sawit selama ini dimanfaatkan sebagai bahan bakar boiler untuk menghasilkan energi mekanik dan panas pada penggilingan minyak kelapa sawit (CPO), menyisakan abu cangkang sawit yaitu sekitar 15% dari berat total cangkang sawitnya. Abu dari sisa pembakaran pada boiler berupa abu dibuang dekat pabrik sebagai limbah padat yang tidak dimanfaatkan. Limbah crumb rubber dan abu cangkang sawit ini dapat dikembangkan dengan membuat Vulkanisat dan Barang jadi Handgrip Rubber sepeda motor berbasis Styrene Butadiene. Pembuatan kompon vulkanisat Hand grip Rubber dengan menggunakan Lima perlakuan variasi abu cangkang sawit dan zeosil sebagai bahan pengisi sekaligus berfungsi sebagai penguat dengan 5 perlakuan dan 4 perlakuan variasi limbah padat Crumb rubber dan SBR dalam pembuatannya ada penambahan bahan kimia lainnya diperoleh hasil yang terbaik dengan menggunakan kompon formula 4 yaitu dengan penambahan Limbah Crumb Rubber 70 phr, SBR 30 phr dan Abu Cangkang Sawit 45 phr dengan Zeosil 15 phr serta dan pengujian secara visual. Formulasi Kompon 4 memenuhi persyaratan untuk pengujian fisik dan mekanik yaitu kekerasan yaitu 67,67 shore A dan pengujian Kekerasan After Aging sama yaitu 67,33 shore A; kekuatan tarik 71.59 kg/cm 2 , setelah aging, Elongation at Break (Perpanjangan Putus), % yaitu 388%, after Aging yaitu 360%. Untuk produk jadi hand grip rubber hasil dilakukan pengujian Visual dari 5 Panelis lebih menyukai Hand Grip rubber yang dibuat dari Formula K4. Formulasi kompon 4, modal tetap per bulan Rp 2.630.000,-dan total biaya variabel sebesar Rp 34.180.000,-per bulannya. Rp 25.200.000 kapasitas produksi per bulan, 30.000 kg, menghasilkan 201.000 buah Hand grip Rubber per bulan dan harga jual Rp 6.000,-BEP unit 974 unit Handgrip Rubber, waktu Pengembalian investasi 5,5 bulan. Kata kunci : Bahan pengisi, Abu cangkang sawit, ziosil, limbah karet, crumb rubber, SBR, handle grip rubber.
Nanosilika sekam padi dapat digunakan sebagai bahan pengisi alternatif dalam pembuatan vulkanisat karet. Penelitian ini bertujuan untuk mengetahui pengaruh nanosilika sekam padi terhadap sifat mekanik dan reologi vulkanisat karet dan dibandingkan dengan bahan pengisi carbon black pada pembuatan vulkanisat karet. Pengaruh konsentrasi nanosilika sekam padi (10, 20, 30, 40 dan 50 phr) pada masing-masing konsentrasi terhadap kekerasan, pampatan tetap, modulus 300%, modulus torsi, laju pemasakan optimum, dan waktu scorch. Penelitian eksperimental menggunakan Rancangan Acak Lengkap non Faktorial dan setiap perlakuan diulang sebanyak tiga kali. Hasil pengujian mekanis dan reologi menunjukkan tren dan tidak ada perbedaan nilai yang signifikan antara nanosilika sekam padi dan carbon black yang digunakan sebagai bahan pengisi. Perlakuan terbaik diperoleh pada konsentrasi nanosilika sekam padi 30 phr, dan konsentrasi carbon black 40 phr. Vulkanisat karet dengan bahan pengisi carbon black menunjukkan kekerasan, modulus 300%, modulus torsi yang lebih tinggi, namun laju pemasakan optimum, pampatan tetap, dan waktu scorch lebih rendah dari pada nanosilika sekam padi. Nanosilika sekam padi dapat menjadi pengganti carbon black yang baik untuk produk-produk karet dengan biaya dan pampatan tetapnya dipersyaratkan.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.