In this study we examine the potential for using brushite (dicalcium phosphate dihydrate) as a coating for orthopedic implants. It was found that brushite is transformed into a more stable calcium phosphate (hydroxyapatite), regardless of the aqueous transforming media utilized. The transformation was carried out at room temperature in deionized water, deionized water with added calcium ions, and modified Hank's type solution without calcium and magnesium ions, modified Hank's type solution with calcium and magnesium ions, and modified Hank's type solution with added calcium ions. In several of the transformation systems it was noted that brushite provided an increased amount of calcium ions to the transforming media through solubility. The process was monitored using X-ray diffraction, X-ray photoelectron spectroscopy, and dissolution studies. Scanning electron microscopy and energy dispersive spectroscopy were also utilized for characterization. The brushite coatings can be easily achieved electrolytically on conducting substrates. The process is non line of sight, simple, and inexpensive; and when using an electrolyte that can sustain currents of approximately 100 mA/cm2, the necessary coating can be completed in about 3 min.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.