CIGS thin films were deposited on soda lime glass by one-step magnetron sputtering using a single quaternary-CIGS target in stoichiometric proportions. The influences of substrate temperature on the structural, optical, and electrical properties of Cu(In,Ga)Se2 (CIGS) thin films were investigated. The phase structure of CIGS thin films was characterized by X-ray diffraction (XRD). The morphology and thickness of CIGS thin films were observed by Scanning Electron Microscope (SEM). The absorption coefficient of CIGS thin films was measured by Ultraviolet-visible Spectrophotometer. Four-point probe method was used to test the resistivity of CIGS thin films. Based on the results of characterization, the increase in crystallite size of CIGS was found to be significantly noticeable with increasing substrate temperature. UV-vis measurement analysis suggested that CIGS thin films deposited at different substrate temperatures had high absorption coefficient (~104 cm-1) and optical band gap (1.07-1.23 eV). The substrate temperature dependence of the resistivity of the films indicated that the resistivity of the films fall to about 0.5 Ω۰cm as the substrate glass was heated up to 300 °C.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.