BaTiO3–(Bi1/2Na1/2)TiO3(abbreviated as BT-BNT) solid solution ceramics, as a lead-free PTC (Positive Temperature Coefficient of resistivity) thermistor material usable over 130°C, were synthesized in air atmosphere. By conventional processes, La-doping was not effective in giving semiconducting property to the BT-BNT ceramics because of volatilization of sodium and bismuth during sintering. By preventing the volatilization by lowering the sintering temperature using very fine TiO2powder and by adding calcium oxide to calcined BT-BNT powders, we obtained BT-BNT semiconducting ceramics which shows a resistivity change near Curie temperature.
BaTiO3–(Bi1/2K1/2)TiO3 (abbreviated as BT-BKT) solid solution ceramics, as a lead-free PTC (positive temperature coefficient of resistivity) thermistor material usable over 130°C, has been synthesized by sintering in N2 atmosphere and after annealing in air over 1200°C. In the BT-BKT ceramics with PTC property, the impedance/modulus spectroscopic plots have revealed that a third resistance-capacitance (RC) response besides grains and grain boundaries. Using the remote electron beam induced current (REBIC) configuration, imaging has revealed EBIC contrast consistent with the presence of negatively charged electrostatic grain boundary barriers in the BT-BKT semiconducting ceramics.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.