A series of novel polyurethane/siloxane-based wound dressing membranes was prepared through sol-gel reaction of methoxysilane end-functionalized urethane prepolymers composed of castor oil and ricinoleic methyl ester as well as methoxysilane functional aniline tetramer (AT) moieties. The samples were fully characterized and their physicochemical, mechanical, electrical, and biological properties were assayed. The biological activity of these dressings against fibroblast cells and couple of microbes was also studied. It was revealed that samples that displayed electroactivity by introduction of AT moieties showed a broad range of antimicrobial activity toward different microorganisms, promising antioxidant (radical scavenging) efficiency and significant activity for stimulation of fibroblast cell growth and proliferation. Meanwhile, these samples showed appropriate tensile strength and ability for maintaining a moist environment over a wound by controlled equilibrium water absorption and water vapor transmission rate. The selected electroactive dressing was subjected to an in vivo assay using a rat animal model and the wound healing process was monitored and compared with analogous dressing without AT moieties. The recorded results showed that the electroactive dressings induced an increase in the rate of wound contraction, promoted collagen deposition, and encouraged vascularization in the wounded area. On the basis of the results of in vitro and in vivo assays, the positive influence of designed dressings for accelerated healing of a wound model was confirmed.
A novel biodegradable electroactive polyurethane containing aniline pentamer (AP) was blended with polycaprolactone (PCL). The prepared blend (PB) and PCL were further fabricated in to scaffolds using a mixture of poly(ethylene glycol) and salt particles in a double porogen particulate leaching and compression molding methodology. Scaffolds held open and interconnected pores having pore size ranging from several μm to 150 µm. PB scaffolds had compression modulus and strength of 4.1 and 1.3 MPa, respectively. The conductivity of the scaffold was measured as 10(-5) ± 0.09 S .cm(-1) and preserved for at least 100 h post fabrication. Scaffolds supported neonatal cardiomyocytes adhesion and growth with PB showing more extensive effect on the expression of the cardiac genes involved in muscle contraction and relaxation (troponin-T) and cytoskeleton alignment (actinin-4). Our results highlight the potential of incorporation of AP as an electroactive moiety for induction of cardiomyocyte proliferation and repair of damaged heart tissue.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.