Recently, Fe-based perovskite oxides, such as Ln1-xSrxFeO3-δ (Ln = La, Pr, Nd, Sm, Eu) have been proposed as potential alternative electrode materials for solid oxide fuel cells (SOFCs), due to their good phase stability, electrocatalytic activity, and low cost. This work presents the catalytic effect of BaCO3 nanoparticles modified on a cobalt-free La0.8Sr0.2FeO3-δ-Gd0.2Ce0.8O2-δ (LSF-GDC) composite cathode at an intermediate-temperature (IT)-SOFC. An electrochemical conductivity relaxation investigation (ECR) shows that the Kchem value of the modified LSF-GDC improves up to a factor of 17.47, demonstrating that the oxygen reduction process is effectively enhanced after surface impregnation by BaCO3. The area-specific resistance (ASR) of the LSF-GDC cathode, modified with 9.12 wt.% BaCO3, is 0.1 Ω.cm2 at 750 °C, which is about 2.2 times lower than that of the bare cathode (0.22 Ω.cm2). As a result, the anode-supported single cells, with the modified LSF-GDC cathode, deliver a high peak power density of 993 mW/cm2 at 750 °C, about 39.5% higher than that of the bare cell (712 mW/cm2). The single cells based on the modified cathode also displayed good performance stability for about 100 h at 700 °C. This study demonstrates the effectiveness of BaCO3 nanoparticles for improving the performance of IT-SOFC cathode materials.
Proton-conducting solid–oxide fuel cell (H-SOFC) is an alternative promising low-temperature electrochemical cell for renewable energy, but the performance is insufficient because of the low activity of cathode materials at low temperatures. A layered perovskite oxide PrBaFe1.9Zn0.1O5+δ (PBFZ) was synthesized and investigated as a promising cathode material for low-temperature H-SOFC. Here, the partial substitution of Fe by Zn further enhances the electrical conductivity and thermal compatibility of PrBaFe2O5+δ (PBF). The PBFZ exhibits improved conductivity in the air at intermediate temperatures and good chemical compatibility with electrolytes. The oxygen vacancy formed at the PBFZ lattice due to Zn doping enhances proton defects, resulting in an improved performance by extending the catalytic sites to the whole cathode area. A single cell with a Ni-BZCY anode, PBFZ cathode, and BaZr0.7Ce0.2Y0.1O3-δ (BZCY) electrolyte membrane was successfully fabricated and tested at 550–700 °C. The maximum power density and Rp were enhanced to 513 mW·cm−2 and 0.3 Ω·cm2 at 700 °C, respectively, due to Zn doping.
The effects of the electrochemical oxygen reduction reaction (ORR) on the surface of single-phase perovskite cathodes are well understood, but its potential for use in a complex system consisting of different material types is unexplored. Herein, we report how BaCO3 nanoparticles-modified La0.6Sr0.4Co0.2Fe0.8O3-δ-Gd0.2Ce0.8O2-δ (LSCF–GDC)-composite cathodes improved the electrochemical oxygen reduction kinetics for high-performing ceramic fuel cells. Both X-ray diffraction (XRD) and thermogravimetric analysis (TGA) studies reveal that BaCO3 is stable, and that it does not show any solid-state reaction with LSCF–GDC at SOFCs’ required operating temperature. The electrochemical conductivity relaxation (ECR) study reveals that during the infiltration of BaCO3 nanoparticles into LSCF–GDC, the surface exchange kinetics (Kchem) are enhanced up to a factor of 26.73. The maximum power density of the NiO-YSZ anode-support cell is increased from 1.08 to 1.48 W/cm2 via surface modification at 750 °C. The modified cathode also shows an ultralow polarization resistance (Rp) of 0.027 Ω.cm2, which is ~4.4 times lower than that of the bare cathode (~0.12 Ω.cm2) at 750 °C. Such enhancement can be attributed to the accelerated oxygen surface exchange process, possibly through promoting the dissociation of oxygen molecules via the infiltration of BaCO3 nanoparticles. The density functional theory (DFT) illustrates the interaction mechanism between oxygen molecules and the BaCO3 surface.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.