The effect of specimen thickness on the creep response of Ni-based single-crystal superalloy DD6 was investigated. With the thickness of 0.3 mm, 0.6 mm and 1.2 mm, a series of thin-wall specimens were tested in this paper respectively at 760℃, 980℃ and 1,100℃. Under the conditions of lower temperatures and higher stresses, the creep life of thin-wall specimens increases with the increase of δ, but it is almost equal under higher temperatures and lower stresses conditions. Compared with the standard specimens, an obvious reduction (about 60%) of creep life of the thin-wall specimens was found at 760℃, whereas it is almost the same at 980℃ and 1,100℃. Therefore, obvious thickness effect is prone to lower temperature and higher stress. The thickness effect is a comprehensive effect, which is caused by fracture mode, the degree of necking, the shape and quantity of creep cavities, oxide thickness, etc. Under each condition, an increased thickness resulted in increased creep strain to rupture.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.