Zinc–Magnesium (Zn–Mg) alloy as a novel biodegradable metal holds great potential in biodegradable implant applications as it is more corrosion resistant than Magnesium (Mg). However, the mechanical properties, biodegradation uniformity, and cytotoxicity of Zn–Mg alloy remained as concerns. In this study, hot extrusion process was applied to Zn–1 wt % Mg (Zn–1Mg) to refine its microstructure. Effects of hot extrusion on biodegradation behavior and mechanical properties of Zn–1Mg were investigated in comparison with Mg rare earth element alloy WE43. Metallurgical analysis revealed significant grain size reduction, and immersion test found that corrosion rates of WE43 and Zn–1Mg were reduced by 35% and 57%, respectively after extrusion. Moreover, hot extrusion resulted in a much more uniform biodegradation in extruded Zn–1Mg alloy and WE43. In vitro cytotoxicity test results indicated that Zn–1Mg alloy was biocompatible. Therefore, hot extruded Zn–1Mg with homogenous microstructure, uniform as well as slow degradation, improved mechanical properties, and good biocompatibility was believed to be an excellent candidate material for load-bearing biodegradable implant application.
The presence of a hierarchical channel network in tissue engineering scaffold is essential to construct metabolically demanding liver tissue with thick and complex structures. In this research, chitosan–gelatin (C/G) scaffolds with fine three-dimensional channels were fabricated using indirect solid freeform fabrication and freeze-drying techniques. Fabrication processes were studied to create predesigned hierarchical channel network inside C/G scaffolds and achieve desired porous structure. Static in-vitro cell culture test showed that HepG2 cells attached on both micro-pores and micro-channels in C/G scaffolds successfully. HepG2 proliferated at much higher rates on C/G scaffolds with channel network, compared with those without channels. This approach demonstrated a promising way to engineer liver scaffolds with hierarchical channel network, and may lead to the development of thick and complex liver tissue equivalent in the future.
Mg-based biodegradable implants offer several advantages over their non-degradable or degradable polymeric counterparts used today. However, the low corrosion resistance of Mg in physiologic environment remained as concerns. In this research, nanodiamond (ND) was uniformly dispersed in Mg matrix to induce a protective layer on Mg surface during corrosion. Compared with pure Mg, fabricated Mg-ND nanocomposites had lower corrosion rates, higher corrosion potential, and higher corrosion resistance. Specifically, the corrosion rate of Mg was reduced by 4.5 times by adding 5 wt% of ND particles. Corrosion inhibition effect of ND was thus validated. The chemical interaction and physical adsorption of the ions from simulated body fluid on ND might be the main reason for enhanced corrosion resistance. In vitro biocompatibility test results indicated that Mg-ND nanocomposites were biocompatible since cells growing in contact with corrosion products of Mg-ND maintained high cell viability and healthy morphology. Therefore, Mg-ND nanocomposites with homogenous ND dispersion, enhanced corrosion resistance, and good biocompatibility might be an excellent candidate material for biodegradable implant application.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.