We have investigated the adsorption of CO and CO2 on epitaxially grown Cr2O3(111) by means of EELS. LEED, ARUPS, NEXAFS and XPS. CO is found to adsorb on the oxide surface in an ordered (√3 × √3)R30° structure with the molecular axis oriented approximately parallel to the surface. CO2 on the other hand reacts with the chromium oxide to form a surface carbonate. Adsorption of CO, respectively reaction of CO2 only takes place on a clean, freshly flashed oxide surface. Preadsorption of oxygen leads to a surface which is rather inert to adsorption, likely due to electronic or steric reasons.

Butane activation has been studied using three types of sulfated zirconia materials, single crystalline epitaxial films, nanocrystalline films, and powders. A surface phase diagram of zirconia in interaction with SO(3) and water was established by DFT calculations, which was verified by LEED investigations on single-crystalline films and by IR spectroscopy on powders. At high sulfate surface densities a pyrosulfate species is the prevailing structure in the dehydrated state; if such species are absent, the materials are inactive. Theory and experiment show that the pyrosulfate can react with butane to give butene, H(2)O and SO(2), hence butane can be activated via oxidative dehydrogenation. This reaction occurred on all investigated materials; however, isomerization could only be proven for powders. Transient and equilibrium adsorption measurements in a wide pressure and temperature range (isobars measured via UPS on nanocrystalline films, microcalorimetry and temporal analysis of products measurements on powders) show weak and reversible interaction of butane with a majority of sites but reactive interaction with <5 micromol g(-1) sites. Consistently, the catalysts could be poisoned by adding sodium to the surface in a ratio S/Na = 35. Future research will have to clarify what distinguishes these few sites.