Carbides, borides and nitrides of high melting transition metals were synthesized by high energy ball milling of elemental powder mixtures. The obtained hard material phases show a nanocrystalline structure with a saturation value of the crystal sizes between 7-8 nm. The kinetics of the reaction were investigated, and the nanocrystalline powders were densified by HIP.
The dislocation velocity, %, in basal slip shows a maximum within the range of homogeneit y of the Laves phase MgZn,. The temperature dependence of can be described by an thermaIly activated mechanism with an activation enthalpy of (1.7 If. 0.3) eV in agreement with macroscopic deformation experiments.Die Versetzungsgeschwindigkeit j . fur Basisgleitttng der Laves-Phase MgZn, zeigt innerhalb des Homogenitiitsbereiches ein Maximum bei der stochiometrischen Zusammensetzung. Die Temperaturabhiingigkcit von kann durch einen thermisch aktivierbaren Mechanismus mit einer Aktivierungsenthalpie von (1,7 rf: 0,3) eV in Ubereinstimmung mit makroskopischen Verformungsexperimenten beschrieben wcrden.
Der im Homogenitätsbereich der intermetallischen Verbindung MgZn2 beobachtete Effekt der Legierungsentfestigung erweist sich nach Vergleich mit Messungen der Versetzungsgeschwindigkeit und der Versetzungsdichte als durch Versetzungsdichteänderung hervorgerufen.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.