Defect free copper welds were achieved by friction stir welding (FSW) carried out at a constant welding speed of 100 mm min 21 . The influence of tool rotation rate on microstructure, mechanical properties and fracture location was investigated. As the tool rotation rate increased, the grains of nugget zone grew significantly, the thermomechanically affected zone became indistinct and the grain size increased, but the effect of tool rotation rate on the grain size of heat affected zone was limited. Both ultimate tensile strength (UTS) and elongation increased first and then decreased with increasing rotation rate and the UTS achieved a highest value of 282 MPa at the rotation rate of 400 rev min 21 together with the welding speed of 100 mm min 21 , which was on the level of the base metal. The fracture occurred at the cavity defect on the advancing side of the joint when the FSW was performed at a low tool rotation rate, while it occurred on the retreating side when the tool rotation rate was relatively high.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.